Refractory Fireclay Brick for Pizza Oven

Name: Refractory Fireclay Brick for Pizza Oven
Brand: Hebei DFL Minmet Refractories Corp.
Rating: 4.3 (2 reviews)

Get Latest Price

Send Inquiry

Model No. :	SK
Brand Name :	D-FB

3yrs

ShiJiaZhuang, Hebei, China

Visit The Store

Hebei DFL Minmet Refractories Corp.

VISIT THE STORE

Product description

1. standard size: 230x114x65/75mm
2. refractoriness: from 1670 to 1810
3. kiln car refractory brick
4. ASTM & JIS standard

Refractory fireclay brick refers to fire brick containing Al2O3 less than 48%, which is made of high grade bauxite through high temperature calcinations. High alumina brick is a kind of neutral refractory material so that it enjoys excellent resistance to acid and alkali corrosion. It has characteristic of high refractoriness under load, which decide high alumina brick is a n ideal material for various kinds of industrial furnace. It is widely used in building lining of hot-blast stove, blast furnace, coke oven, rotary kilns of cement and so on.

characteristics: 1 Excellent thermal stability
                       2 High refractoriness under load
                       3 Chemical stability and anti-corrision
                       4 Small high temperature creep rate
                       5 Excellent thermal shock resistance

Typical Application: 1 Building materials for blast furnace
                               2 Building materials for hot-blast stove
                               3 Building materials for coke oven
                               4 Building materials for steel making furnace

5.Building materials for wood oven

6 Kiln car building
7 For ladle and refining furnace

8. For aod furnace

9. For pizza oven building.

Product Type: fireclay brick (SK 32, SK 34)
high alumina brick (sk 35-38)

Package: pallet, thermal shrinkage package

Product grade	SK-32	SK-34	SK-35	SK-36	SK-37	SK-38
Al2O3	30 MIN	40 MIN	48 MIN	60 MIN	70 MIN	80 MIN
Fe2O3	3 MAX	2.5MAX	2.0MAX	2.0 MAX	2.0 MAX	2.0MAX
Refractories, deg C	1730 min	1750 min	1750 min	1790 min	1790 min	1790Mn
Refractories under load	1350C min	1400C min	1420C min	1500C min	1500C min	-
Bulk density g/cm3	2.0-2.10	2.10-2.20	2.15-2.25	2.5-2.6	2.55-2.65	2.75 min
Apparent porosity %	24 max	22 max	22 max	22 max	22 max	22 max
Cold crushing strengh, Mpa	25 min	30 min	39 min	80 min	60 min	80 min
We confirmed Bulk density g/cm3	2.05	2.15	2.2	2.55	2.6	2.7