JL-25E Self-crossing Styrene-acrylate Copolymer Emulsion

Specifications 1. With self-crosslinking founction

2. High glossy

3. Good water resistance

4. Good Scratch resistance

    JL-25E Styrene-acrylate copolymer emulsion   Product introduction:   The emulsion is prepared by using styrene and acrylic acid as main raw material and introducing acrylamide monomer ,has superior performances than other styrene-acrylic emulsion such as degree of light ,adhesion, water and solvent resistance ,abrasion resistance. With the wax emulsion compound, it can be prepared with different uses high performance paper Polish oil.     Features: 1. With self-crosslinking founction 2. High glossy 3. Good water resistance  4. Good Scratch resistance     Applications: 1. Paper polilsh finishing 2. Mortar printing     Application guideline 1. Adding suitable coupling agent for different substrates can enhance film properties 2. Painting method: spraying, dip coating etc 3. Curing conditions: 60~80°C, 1~2 mins 4. Suitable substratees: Paper, various types of textiles, etc 5. No need to mix curing agent cause iJL-25E has self-crossing function   Formula advices:

Material	Quantity/g
JL-25E	97
Wax Emulsion	2
Defoaming agent	0.1-0.2
Thickening agent	0.1-0.2
Wetting agent	0.1-0.2
Leveling agent	0.1-0.2

  Film performances: (60°C, 2 minutes )  

Testing item	Testing method	Result
Appearance	Visual observation	Good fullness
Gloss	60°C gloss meter	≥80°
Adhesion	100 grid test	1 class
Tensile rate	Tensile test method	≥50%
Water Resistance	Dipping	≥48h
Boiling water resistance	Boiling at 100°C	≥1h
Ethanol Resistance	Dipping	≥6h

      Package and storage: Packaging:50KG, 100KG plastic drum Strage: Stored in air light containers, refrain from moisture, high temperature;              Stored at dark, cool and dry place of 5~30°C;                      Material safety: The MSDS of the product will be provided upon the client’s request