UNS N05500 Monel K500 Ring

Specifications Monel K500 Ring

Wire: 0.3mm-8mm

Bar: 10mm-200mm

Ring: OD50mm-300mm*ID 30mm-260mm

  Monel K500 bar       Forging Disc     Strip   Monel K-500 Chemical composition:

Alloy	%	Ni	Cu	Al	Ti	Fe	Mn	S	C	Si
Monle K500	Min.	63	27.0	2.30	0.35
	Max.		33.0	3.15	0.85	2.0	1.5	0.01	0.25	0.5

Monel K-500 Physical properties:

Density	8.44 g/cm3
Melting point	1315-1350°C

Monel K-500 minimum mechanical properties in the room temperature:

Forms	Condition	Max. section Thickness,in.(mm)	Tensile strength Min. Ksi.(Mpa)	Yield strength Min.Ksi.(Mpa)	Elongation in 2 in,or 4D,min.,%	Hardness
						HB min.	HRC min.
Round bars, Hexagons, squares, rectangles and forgings	hot-worked and age hardened	All Sizes	140(965)	100(690)	20	265	27
Round bars	cold worked and age hardened	1/4(6.4)to 1(25.4)	145(1000)	110(760)	15	300	32
		over 1(25.4)to 3(76.2)	140(965)	100(690)	17	280	29
		over 3(76.2)to 4(101.6)	135(930)	99(655)	20	255	25
Hexagons	cold worked and age hardened	1/4(6.4)to 2(50.8)	140(965)	100(690)	15	265	27
Round bars, Hexagons, squares, rectangles and forgings	Annealed and age hardened	Up to 1(25.4)	130(895)	90(620)	20	250	24
		1(25.4)and over	130(895)	85(585)	20	250	24

Alloy K-500 has approximately twice the tensile strength and triple the yield strength of Alloy 400. The strength of Alloy K-500 is maintained to 1200 degrees Fahrenheit, but stays ductile and tough down to temperatures of -400 degrees Fahrenheit. Alloy K-500 also stays non-magnetic to -200 degrees Fahrenheit.
Additional characteristics of Alloy K-500 include outstanding corrosion resistance in a wide range of chemical and marine surroundings, from salts and alkalis, non-oxidizing acids to pure water. Alloy K-500 is non-magnetic and spark resistant. It is also recommended that Alloy K-500 be annealed when it is welded and that any weldments be stress relieved prior to aging. Industries Served: gas & oil extraction chemical processing marine engineering