1 / 6
Model No. : | TPM-I |
---|---|
Brand Name : | Shanxi Changda |
Product description
Density /g/cm3 | 2.02 |
Softening Point/°C | 103 |
Color and appearance of coating film | After drying , no wrinkle, spot , falling off, sticking to the wheel .And the color and shape of coating has not large differences to standard plate |
Cure time /minutes | 3 |
Chromaticity Coordinates/(x,y) | X:0.318 Y:0.337 |
Compressive Strength/Mpa | 15.4 |
Luminance Factor | 0.80 |
Abrasion Performance/mg(200r/1000g reduce weight) | 55.2 |
Content of glass beads(%) | 22.6 |
Flow resistance | 39 |
Low temperature Anti-cracking of coating layer | Keep 4h in -10°C ,and lay 4h in normal temperature as a circulation .And continuously do three circulations , no crack |
Heating stability | Keep 4h in 200~220°Cin agitating condition, no obviously yellowing, burnt , blocked |
Density /g/cm3 | 1.95 |
Viscosity | 139 |
Color and appearance of coating film | After drying , no wrinkle, spot , falling off, sticking to the wheel .And the color and shape of coating has not large differences to standard plate |
Cure time /minutes | 10 |
Cover Rate(%) | 98 |
Chromaticity Coordinates/(x,y) | X:0.311 Y:0.328 |
Compressive Strength/Mpa | 13.9 -- 23°C±1°C 2.4 -- 50°C±2°C |
Luminance Factor | 0.83 |
Abrasion Performance/mg(200r/1000g reduce weight) | 21.5 |
Anti-watering | No abnormal phenomenon dunking in water for 24h |
Anti-alkali | No abnormal phenomenon dunking in calcium hydroxide saturated solution for 24h |
Flexibility/mm | 1 |
Solid Content/% | 71.2 |