XC-9080W: preheated at 80~100℃ for 6~8 hours XC-6088: preheated at 80~100℃ for 6~8 hours
Items
A/B Materials Temperatures(℃)
A+C/B Mix ratio
(By weight)
Cream Time (s)
End of Rise
Time (s)
Free Rise Foam
Density(g/cm3)
Mold
Temperature(℃)
Demold
Time(min)
Parameter
40~45/38~42
100/105~120
6~8
30~40
0.17~0.21
45~55
3~5
The adding content of C-2 should be 210g±10g/18kg The adding content of water should be 0~90g/18kg according to the reality The adding content of hardener should be 0~1200g/18kg according to the reality
Items
Molded Density (g/cm3)
Hardness
(Shore A )
Tensile strength
(MPa)
Elongation
(%)
Tear Strength
(kN/m)
Williams abrasion
(cc/php)
Physical properties
0.35~0.45
70~90
4~7
200~300
11~20
130~200
Demold time may be prolonged with the increase of sole thickness These physical data are acquired by testing a sample of 6mm thick. Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.