Product description
Descriptions:- Glass fiber is widely used in nylon reinforcement, while there will be glass fiber rich surface/glass emergence on surface problem, dendritic polymer CYD-PR121 is a new surface fiber appearance promoting agent, with good glass fiber dispersion, lubricity and brings excellent mechanical properties to nylon
Index:
- State: Powder at room temperature
- Volatile content,%: ≤2
- MW: around 2,000g/mol
- Hydroxyl value, mg KOH/g: 400-600
- Temperature tolerance: <260℃
Applicable performance:
- Dendritic polymer CYD-PR121 is a great promoting agent of polyamide due to its unique structure and physical property
- Good compatibility in PA, PC, PBT
- Glass fiber can be well coated to prevent appearance in nylon
- Lubricate system and reduce mechanical wear
- Lower processing temperature and endow nylon with great mechanical properties
- Bring nylon product bright surface
Applications:- Used to disperse glass fiber, carbon fiber and other inorganic filler filled material and also to improve mechanical properties, mainly used in auto parts, machine parts, and other aerospace parts
Usage:
- Dried at room temperature of 80°C in vacuum condition for 5h and 12h respectively
- Dosage should be adjusted according to requirement and performance during granulation or processing with PA resin, normally obvious improvement can be achieved by dosage of 0.1-1.5%.
- PA modifier should be mixed uniformly with PA, especially when dosage is
Glass fiber is widely used in nylon reinforcement, while there will be glass fiber rich surface/glass emergence on surface problem, dendritic polymer CYD-PR121 is a new surface fiber appearance promoting agent, with good glass fiber dispersion, lubricity and brings excellent mechanical properties to nylon
State: Powder at room temperature
Volatile content,%: ≤2
MW: around 2,000g/mol
Hydroxyl value, mg KOH/g: 400-600
Temperature tolerance: <260℃
Dendritic polymer CYD-PR121 is a great promoting agent of polyamide due to its unique structure and physical property
Good compatibility in PA, PC, PBT
Glass fiber can be well coated to prevent appearance in nylon
Lubricate system and reduce mechanical wear
Lower processing temperature and endow nylon with great mechanical properties
Bring nylon product bright surface
Used to disperse glass fiber, carbon fiber and other inorganic filler filled material and also to improve mechanical properties, mainly used in auto parts, machine parts, and other aerospace parts
Dried at room temperature of 80°C in vacuum condition for 5h and 12h respectively
Dosage should be adjusted according to requirement and performance during granulation or processing with PA resin, normally obvious improvement can be achieved by dosage of 0.1-1.5%.
PA modifier should be mixed uniformly with PA, especially when dosage is