Incoloy 800h Nickel Alloy Pipe Monel400 Grade For Petrochemical

 

Incoloy 800H Nickel Alloy Pipe MONEL400 Grade For Petrochemical

 

Quick Details 

UNS N08800 / W.Nr. 1.4876
ASTM, ASME, BS, VdTUV, ISO
OD: 10 - 325mm
WT: 1.0 - 30mm
Length: up to 12m

 

Description:

Incoloy 800HT is an iron-nickel-chromium alloy having the same basic composition as Alloy 800, with significantly higher creep rupture strength.

The higher strength results from close control of carbon, aluminum and titanium contents in conjunction with a high temp anneal.

Size: OD 6-219mm, WT:0.5mm-18mm

Density: 8.0g/cm3

Standards: ASTM B407,ASTM B829 ,ASTM B163
Exported country: Spain, Argentina, Canada, Germany, Norway, India    

 

chemical analysis of Incoloy 800HT
C	Cr	Ni	Ti	Al	Fe	Al + Ti	Grain
0.06 -0.10	19.0 -23.0	30.0 - 35.0	0.25 - 0.60	0.25- 0.60	39.5 min	0.85-1.20	5 or coarser

 

Specifications
Sheet/plate	Round bar	Welded Pipe	Seamless Tube	Fittings	Forgings
ASME SB-409 AMS 5871	ASME SB-408 AMS 5766	ASME SB-514 ASME SB-515 ASMES SB-751 ASME SB-775	ASME SB-407 ASME SB-829 ASME SB163	ASME SB-366	ASME SB-564 AMS 5766

Applications:

• Ethylene furnace quench boilers
• Hydrocarbon cracking
• Valves, fittings and other components exposed to corrosive attack from 1100-1800° F
• Industrial furnaces
• Heat-treating equipment
• Chemical and petrochemical processing
• Super-heater and re-heaters in power plants
• Pressure vessels
• Heat exchangers

 

Specifications:

O.D.: 19-325mm
W.T. 1.5-10mm
Grade:N6,MONEL400,INCONEL 600,601,690,INCOLOY 800,800H,825,221,AL904L

INCOLOY 800H SEAMLESS ALLOY TUBE

O.D.: 19-325mm

W.T. 1.5-10mm

Grade:N6,MONEL400,INCONEL 600,INCONEL 601,690,INCOLOY 800,INCOLOY 800H,INCOLOY 825,221,AL904L,718

Standard:ASTM B161-00,ASTM B163-01, ASTM AB165-96,ASTM B167-01,ASTM B407-96, ASTM B423-99,ASTM B423-99,ASTM B649, ASTM B670

 

Pacakge: wooden crate

 

Competitive Advantage:

• Resistant to seawater and steam at high temperatures
• Excellent resistance to rapidly flowing brackish water or seawater
• Excellent resistance to stress corrosion cracking in most freshwaters
• Particularly resistant to hydrochloric and hydrofluoric acids when they are de-aerated
• Offers some resistance to hydrochloric and sulfuric acids at modest temperatures and concentrations, but is seldom the material of choice for these acids
• Excellent resistance to neutral and alkaline salt
• Resistance to chloride induced stress corrosion cracking
• Good mechanical properties from sub-zero temperatures up to 1020^o F
• High resistance to alkalis