HDPE PE 100 Pipe for Water Supply (Roller)

PE Pipe for Water Supply

Product performance

Corrosion resistant. Polyethylene is inert material. Except for few strong oxidant, this material can resist many chemical matters, no electron chemical corrosion, and do not need corrosion proof layer

Non-poisonous. There are not any heavy metal additives in PE pipe for water supply. It is not easy for PE pipe to be covered with dirt and contaminated by bacterium

Low flow resistance. The interior wall of PE pipe is smooth, the friction coefficient is vey low and the flux of a fluid is very high

No Leakage. PE pipe for water supply adopts fusion connection(thermal fusion or electric fusion), compare with rubber and other machinery connect points, it can not occur the leakage as connect point distorted.

High Ductility. PE pipe for water supply possess high ductility, its extension ration at break

Can not excess 500%. And has strong ability for fit with pipe tank non-uniform setting.

Excellent Flexibility. The flexibility of Polyethylene makes PE pipe for water supply can can be coiled. It is used for no pipe tank construction. Layout PE pipe for water supply depends the demand of construct

Good resistance ability for scratch. Scratch can make material strengthconcentration and cause pipe damage

Resistance to impact. PE pipes are so tough that they do not intend to rupture if heavy presses the pipes directly.

Convenient for Construction. The pipes are light and handled friendly.

Long service life. More than 50 years

PE pipe for water supply performance requirement
Name		Hoop stress    Mpa						Requirements
		PE80		PE100
20°C Hydrostatic strength		9.0		12.4				≥100h No leaks no failure
80°C Hydrostatic strength		4.6		5.5				≥165h No leaks no failure
80°C Hydrostatic strength		4.0		5.5				≥1000h No leaks no failure
Name							Requirements
Elongation at break							≥350%
Heat reversion(110 C)							≤3%
Oxidation induction time							≥20min
Resistance to weathering(for bule pipes only)(Multiplied energy of pipe ≥3.5GJ/M energy resistant to aging)		80C Hydrostatic strength(165h)					No leaks, no failure
		Elongation at break shall be met					≥350%
		Thermal stability(200C)					≥100min
PE80					PE100
Failure stress Mpa		Failure time  h			Failure stress Mpa			Failure time h
4.5		219			5.4			233
4.5		283			5.3			332
4.3		394			5.2			476
4.2		533			5.1			688
4.1		727			5.0			1000
4		1000