Company Profile:
1.Capacity: 100 Pultrusion lines, the largest manufacturer of composite insulator rods in China.
2.Technique: the only one using vacuum injection technique without mould release agent, Patent No.200610041850.1.
3.Test: Rods passed tests in domestic labs, including WHVRI,CEMT,XIHARI, especially passed KEMA tests in the Netherlands and 7200h stress corrosion test.
4.Standards: IEC61109 IEC61952, ANSI C29.13-2000, GB/T19519,DL/T810 DL/T864
5.Application: The rods of Taporel have been applied in the highest voltage(1000kv) AC transmission lines & applied in the highest voltage(±800kv) DC transmission lines.
2. Specifications :
Diameter 5mm-130 mm; Length according to customer's order
3.Classify:
3.1Based on properties, rods are classified into High temperature resistant type (E-glass Rod) and High temperature & acid resistant type (ECR-glass Rod).
3.2Based on properties, rods are classified into High temperature resistant type (E-glass Rod) and High temperature & acid resistant type (E-glass Rod)
3.3Based on application, fiberglass rods are classified into 7 types:
for composite suspension & tension insulators (Diameter 16mm—40mm)
for composite pin insulators((Diameter 24mm---53mm)
for composite cross arm insulators(Diameter 28mm—80mm)
for composite post insulator (Diameter 28mm—130mm)
for composite surge arresters(Diameter 5mm—40mm)
for composite fuse cutout (Diameter 19mm—36mm)
3.3. Color: Light green, brown, black
no
|
parameter
|
unit
|
specification
|
1
|
Density(at 20±2)
|
g/cm 3
|
2.2
|
2
|
Water absorbtion rate (at20±2,24h)
|
%
|
0.05
|
3
|
Tensile strength
|
Mpa
|
1690
|
4
|
Bending strength
|
Mpa
|
1100
|
5
|
Dry penetration test
|
Min
|
50
|
6
|
Water difussion test(1%nacl,boiling for 100h 12kv/1min)
|
μA
|
<10
|
7
|
Shearing strength along laminals
|
Mpa
|
50
|
8
|
Volume resistivity(140,96h)
|
Ω.M
|
10 10
|
9
|
DC withstand voltage(10min)
|
kV
|
50
|
10
|
Lightning surge withstand voltage(100kv,10mm)
|
times
|
5
|
11
|
Bending strength at heating conditions
|
Mpa/150
|
350
|
12
|
Stress corrosion (1 mol/1hno3,at 67% stress)
|
h
|
7200
|
13
|
Torsion strength
|
Mpa
|
800
|