OLV712 Acetic General Purpose Silicone Sealant is one-part room temperature acetoxy silicone sealant. It is widely used, durable general filler for glasses, windows and doors, good adhesion to other common construction materials.
Main purposes:
1. For sealing glasses, windows and doors;
2. For sealing aluminum alloy, ceramic, glass fiber, non-oily wood
Characteristics:
1. One-component, acetic cured.
2. Easy to use, cured quickly, good weatherability;
3. Good adhesion to many building materials;
4. Colors include clear, white, grey and black, or other colors as per customers' requirements.
Application:
1. Clean with solvents such as toluene or acetone to keep the substrate surfaces completely clean and dry;
2. Fully filling the gap for better sealing to the surfaces of the material.
3. For better appearance cover outside of joint areas with masking taps before application;
4. Cut nozzle to desired size and extrudes sealant to joint areas;
5. Tool immediately after sealant application and remove masking tape before sealant skins.
Limitations:
1. Certain corrosion to cement, marble, coated glass, copper, lead, zinc-coated materials.
2. Unsuitable for curtain wall structural adhesive;
3. Unsuitable for the airproof location, because it is required to absorb moisture in air to cure for the sealant;
4. Unsuitable for the frosty or moist surface;
5. Unsuitable for the continually soggy place;
6. Can't be used if the temperature is below 4° C or above 50° C on the surface of the material.
Shelf life: 12 months if keep sealing, and stored below 270C in cool, dry place after the date of production.
Volume: 300ml
OLV3010 Acetic General Purpose Silicone Sealant |
Model No |
3010 |
Testing Method |
Test at 50± 5% RH and temperature 23± 20C: |
Density (g/cm 3 ) |
0.956 |
GB/T 13477 |
Drying Time (min) |
8 |
GB/T 13477 |
Extrusion (ml/min) |
1249 |
GB/T 13477 |
Curing Speed (mm/d) |
3 |
GB/T 13477 |
As Cured -After 21 days at 50± 5% RH and temperature 23± 20C: |
Hardness (shore A) |
25 |
GB/T 531 |
Tensile Strength (Mpa) |
0.28 |
GB/T 13477 |
Elongation of Rupture (%) |
120.3 |
GB/T 13477 |
Movement Capacity |
12.5 |
GB/T 13477 |
Storage |
12 months |
|