FC magnesite bof gunning material refractory for Converter

                                            Gunning Material for Converter     Production Technics:   1.Based on high pure magnesia, as the main raw material;   2.adding various compound anchoring agent, ;   3.By mixing and refining.      Production Features:   1.High refractoriness ,excellent resistance for spall , high tap density    2.Easy to spry and sinter, Adhesive rate reach 94% , low rebounding ;   3.Long service life ,once can last 10-24 hours ;   4.Minimum pollutants      Construction method :   1.using quantity:for 30 tons converter, one ton /time   2.Using method : to fill  Gunning Mass into the spraying tank (compressed air without water under 2.2-0.4pa ); and then spray to the part need to be repair .   3.After spraying , there will be 20 minutes for sintering ;   4.Note: if somewhere occur weak situation,must stick the brick firstly ,and then spray again .      Application:BOF impact ,hot patching repairing .      Quality Table:  

Brand	MgO %	SiO2 %	Fe2O3 %	CaO %	B D g/cm3	C.C.S Mpa (1500°C×2h burnt )
ZMPL-1	≥88	2-4	≤1.0	≤4	2.5	≥12
ZMPL-2	≥87	2-4	≤1.5	≤5	≥2.5	≥12
ZMPL-3	≥85	2-4	≤2.0	≤6	≥2.4	≥10
ZBPL-1	82-86	2-4	≤1.0	6-8	≥2.4	≥10
ZBPL-2	78-82	2-4	≤1.5	8-12	≥2.3	≥10