FC corrundom base Casting mix for Blast furnace main runner

                                               FC corrundom base Casting mix for Blast furnace main runner                             Production Technics:             1.Use the super aluminum bauxite and corundum as bone material,          2.adding anchoring agent, coagulator and water reducing agent at the same time.          3.Made by mixing with super .       Production Feature:            1.Good strength ,better stability ;          2.Resist the spalling and erosion;          3.Improve the ladle life       Main Use:          casting for various blast furnace main runner,can replace the burnt high alumina bricks and fire brick.       Work method :Flowing after casting ,no need to shake.       Quality Table:      

Item		Index
Al2O3                                          %		≥75
Bulk density	110°Cx 24h                   g/cm3	≥2.8
	1450°Cx3h                  g/cm3	≥2.65
ColdBreaking Strength	110°Cx 24h                    Mpa	≥6
	1450°Cx3h                    Mpa	≥8
ColdBreaking Strength	110°Cx 24h                    Mpa	≥45
	1450°Cx3h                    Mpa	≥70
Linear Change	1450°Cx3h                     %	±0.3