Explosive welding copper aluminum composite joint

CHANPIN copper aluminum composite clad

Size:

Less than 15mm thickness, width less than 1000mm, the length is less than or equal to 6000mm.

product characteristics:

The compound strength of the product is high, and the surface recombination between copper and aluminum is realized. Good mechanical properties, can meet the bending, drilling, punching and other processing requirements. The copper plate has the advantages of good conductivity, large transition area of copper and aluminum and smooth transition, and solves the problems of low conductivity and easy fracture of the copper and aluminum joint of the traditional product, and the cost is greatly reduced compared with the traditional process.

Technical parameters :

The composite strength is not less than 12N/mm; composite rate: 100%; shear strength is not less than 35MPa

Tensile strength: 90~150MPa; elongation: 0~35%;

DC resistivity is less than or equal to 0.0245. Mm - /m

The surface conductivity is not less than 98%

Rated current: less than or equal to 65 DEG C temperature rise

Application field of copper aluminum transition plate:

Conductive industry (used for the transition connection between copper and aluminum, such as reactor, motor, transformer outlet contact plate and power fittings, etc.).