42crmo4, 40cr Induction Hardened Bar, Chrome Plated Pneumatic Cylinder Piston Rod

42CrMo4, 40Cr Induction Hardened Bar, Chrome Plated   Pneumatic  Cylinder Piston Rod

 

Induction hardened bar

 

Detailed Product Description

1. Material:CK45,ST52,20MnV6,42CrMo4,40Cr
2. Case depth:1.5mm~2.5mm  Induction hardness:HRC62±2
3. Diameter:6~1000mm
4. length:1000~8000mm
5. ISO9001:2008
6: Ground and chrome plated

 

Detailed Description

1.CHEMICAL COMPOSITION

Material	C%	Mn%	Si%	S%	P%	V%	Cr%
Ck45	0.42-0.50	0.50-0.80	0.04	0.035	0.035
ST52	0.22	1.6	0.55	0.035	0.04
20MnV6	0.16-0.22	1.30-1.70	0.10-0.50	0.035	0.035	0.10-0.20
42CrMo4	0.38-0.45	0.60-0.90	0.15-0.40	0.03	0.03		0.90-1.20
40Cr	0.37-0.45	0.50-0.80	0.17-0.37				0.80-1.10

2.MECHANCIAL PROPERTIES

Material	T.S  N/MM2	Y.S  N/MM2	E%(MIN)	CHARPY	CONDITION
CK45	610	355	15	>41J	NORMALIZE
CK45	800	630	20	>41J	Q + T
ST52	500	355	22		NORMALIZE
20MnV6	750	590	12	>40J	NORMALIZE
42CrMo4	980	850	14	>47J	Q + T
40Cr	1000	800	10		Q + T

3. SUPPLY CONDITION

    Ground  and  chrome plated 

4. CHROME THICKNESS

     20 to 30 micron

5. SURFACE ROUGHNESS

     Ra≤0.2 micron and  Rt≤2 micro

6. TOLERANCES ON DIA

    ISO f7 on the diameter

7.OVALITY

Half of the tolerance ISO f7

8. STRAIGHTNESS

   ≤0.2MM/M

9. SURFACE HARDNESS

   850-1150HV (vickers 100g)

10.COHESION

   No cracks,breaking or detaching after thermic shock(warming up at 300 celsius degrees and cooling 

   in water)

11 .POROSITY

     Test according to ISO 1456/1458 and result yaluation according to ISO 4540 rating 8-10

12 CORROSION RESISTANCE

     Test in natural salt spray according to ASTM B 117-72hours

     Results evaluation according to ISO 4540 RATING 7-10

13. WELDABILITY

      Good

14. PACKING

     Anti rust oil to be applied on material and each rod to be packed in paper sleeve

15. CERTIFICATE

     All certificate related with material heat treatment and plating is required