1, 2344 Steel Mill/Round Steel

Basic Info.
Model No.: 1.2344 H13 4Cr5MoSiV1 SKD61
Technique: Forged
Standard: AISI, ASTM, GB, JIS, DIN
Alloy Or Not: Alloy
Application: Tool Steel Bar, Die Steel Bar
Type: Alloy Steel Bar
Special Use: Mold Steel
Grade: H13/1.2344/SKD61
Surface: Black / Machined
Condition: Hardeness / Annealled
Shape: Round Bar / Plate
MOQ: 5 Tons
Specification: T*1800-2300*L3000-5800
Delivery Time: 15--20days
Payment: T/T or L/C at Sight.
Useing: Mould Steel
Technology: Forged
Export Markets: Global
Additional Info.
Trademark: SanHeXing Mould Steel
Packing: Raw, Raw, Wooden or Customers Requirement
Standard: T*1800-2300*L3000-5800
Origin: Dognguan
Production Capacity: 8000ton/Month
Product Description
HOT FORGED ROUND STEEL BARS 1.2344 H13 4Cr5MoSiV1 SKD61
1.2344/H13 has upper hot intensity and rigidity,; Under the middle temperature, H13 has good tenacity, hot tiredness nature and definite wearable.
H13 also has empty quench under the Ao shi ti temperature condition.
Small distortion after heat treatment and so on.
Hardness
Annealed hardness, shall not exceed 235 Brinell (BHN).
A steel specimen having a thickness no greater than one inch shall exhibit a minimum hardness of 50 HRC, when air cooled, after heating for 30 minutes at 1850° F in a protective atmosphere, or when using a non-protective atmosphere, insure the sample has appropriate oversize allowance.
Ultrasonic Quality
SEP1921-84 GR. 3 CLASS D/D
Advantage
A. Tooling materials to be used in the construction of a die casting die for casting Aluminum, Magnesium and ZA alloys, should be high quality tool steel such as Premium Quality H-13 especially for part designs with critical features or if high production runs are being contemplated.
B. Longer die life.
Premium Quality H13 will yield a higher resistance to heat checking, cracking and die wear caused by the thermal shock associated with the die casting process.