1 / 1
Model No. : | SP788X |
---|---|
Brand Name : | LEED |
Product description
Model | SP7887 |
Solids Content | 70~85% |
Viscosity(Pa·S)(Brookfield HBT,25 ,10rpm) | 40~70 |
Fineness | <20μm |
Screen(BOPP stainless steel) | 250~280 mesh |
Drying | infrared stove,250~300°C/3min rotary dry furnace,220°C/8~10min |
Firing | 760~900°C/1~20seconds |
Dried Thickness | 35±3μm |
Fired Thickness | 25±3μm |
Resistivity (fired thickness) | ≤30mΩ/£ |
Cell Winding(125single crystal silion,180μm) | ≤0.8mm |
Adhesion(single side EVA adhesive tape) | excellent |
Photoelectricity Conversion Efficiency | Monocrystal silicon, average conversion efficiency≥17.7 Polysilicon, average conversion efficiency ≥16.5 |
Thinner | LEED XS-08 |
Main feature | energy conversion efficiency |