Hot Rolled Thickness 20~ 120 Mm Aisi M2 High Speed Tool Steel Flat Bar

 

 

Hot Rolled Thickness 20~ 120 MM AISI M2High Speed Tool Steel Flat Bar

 

 

 

Description:

 

 

1.AISI M2/DIN 1.3343/S6-5-2/ JIS SKH 51/GB W6Mo5Cr4V2 High speed steel fat bar

2.Hot rolled condition, annealing or harden, black or milled surface

3. Hot rolled technology:EAF+LF+VD

4.Ultrasonic test standard: SPE1921-GR3, CLASS E/E 

5.Production leadtime: 7~10 days

6. Chemical composition:

 

 

C	Si	Mn	Cr	Mo	V	W	P	S
0.86-0.94	0.40max	0.45max	3.80-4.50	4.70-5.20	1.70-2.20	5.90-6.70	0.03max	0.03max

 

 

7.Compared grades(based on usage):

 

 

Chinese	American	German	Japanese
GB	AISI	DIN	JIS
W6Mo5Cr4V2	M2	1.3343	SKH51

 

 

 

Applications: 

 

 

M2 HIGH SPEED TOOL STEEL used in the manufacture of various types of general tools, and therefore can be produced under high 

load wear-resistant parts, such as cold extrusion die. Has high hardness, high wear resistance, high 

fever hard, high hardenability and sufficient ductility and toughness, good casting, forging, welding and 

machining performance and tool steel, and thus it occupies and important position.

 

 

 

Specifications:

 

 

Hot rolled condition	Steel plate(mm)			Mill name
	Thickness	Width	Length
	20~120	225~610	2500~4500	Dongbei, TianGong
Forged condition	50~350	305~800	2500~4500	Local mill with 6000tons fluid forged machine

 

 

 

Competitive Advantage:

 

• high strength at elevated temperatures
• good toughness
• high compressive strength
• International general tungsten molybdenum high-ductility high-speed steel. The carbon granule of this
• steel is fine and even, featuring in high ductility, superior cutting performance and good heat plasticity
• Good resistance to abrasions, particularly superior read hardness under 600`C.
• Competitive price
• Fast production leadtime
• All the material are inspected with 3 times to meet the highly standards