1 / 1
Brand Name : | GuoXin |
---|
Product description
Fused Rebonded Magnesia Chrome Brick
Direct-bonded magnesia chrome bricks
Brand
MgO (%)≥
SiO2 (%)≤
Cr2O3 (%)≥
Apparent porosity A.P(%)≤
Bulk density B.D(g/cm3)≥
Compressive strength at room temperature C.C.S MPa≥
0.2Mpa Load softening start temperature RUL(℃) ≥
ZHMGe-12
65
2.5
12
18
3.05
40
1700
ZHMGe-14
62
2.5
14
18
3.05
40
1700
ZHMGe-16
60
2.5
16
18
3.1
40
1700
Semi-rebonded magnesia chrome bricks
Brand | MgO (%)≥ | SiO2 (%)≤ | Cr2O3 (%)≥ | Apparent porosity A.P(%)≤ | Bulk density B.D(g/cm3)≥ | Compressive strength at room temperature C.C.S MPa≥ | 0.2Mpa Load softening start temperature RUL(℃) ≥ |
BDMGe-18 | 55 | 2 | 18 | 16 | 3.15 | 45 | 1700 |
BDMGe-20 | 50 | 2 | 20 | 16 | 3.15 | 45 | 1700 |
Fused rebonded magnesia chrome bricks
Brand | MgO (%)≥ | SiO2 (%)≤ | Cr2O3 (%)≥ | Apparent porosity A.P(%)≤ | Bulk density B.D(g/cm3)≥ | Compressive strength at room temperature C.C.S MPa≥ | 0.2Mpa Load softening start temperature RUL(℃) ≥ |
DMGe-18 | 58 | 1.5 | 18 | 15 | 3.2 | 50 | 1700 |
DMGe-20 | 55 | 1.5 | 20 | 15 | 3.2 | 50 | 1700 |
DMGe-24 | 50 | 1.5 | 24 | 15 | 3.25 | 50 | 1700 |
Magnesite Chrome Refractory Bricks are produced from sintered magnesia and chrome ore by sintering at high temperature. Magnesite Chrome Refractory Bricks have high bulk density and advantages of stronger thermal resistance. Magnesite Chrome Refractory Bricks are widely used for;
cement rotary kilns
glass kiln regenerators
permanent lining of steel furnaces
permanent lining of refining ladles
Dashiqiao Guoxin Refractory Material Co., Ltd. is located in Dashiqiao, Liaoning Province, which is the capital of magnesium in China. The company enjoys superior geographical position, with Beijing-Shenyang Expressway, Shenzhen-Dalian Expressway
Send your inquiry to this supplier