FC Magnesia Ramming Material for EAF

                    Ramming mix for electric furnace                      Production Technics:         1.Based on high purified compound dolomite sand and high purified magnesia,        2.Add magnesia iron sand         3.Adding certain quantity of anchoring agent .       Production Feature:        1.Easy to sinter ;       2.Strong anti-permeability;       3.High refractoriness;       4.Long service life.       Application:       Ramming for the slope and bottom of EAF       Use method :       1.Spread the material in the bottom with thichness of100mm to 150mm and rammed hard,        2.Clean the surface, repeat the ramming work once again      3.Put a piece of steel sheet on the surface to avoid damage on the surface when putting scrap        and hot metal.       Quality Table:  

Brand	MgO %	CaO %	Fe2O3 %	SiO2 %	B D g/cm3	L.C.R % (1500°C×2h)	C.C.S Mpa (1500°C×2h)
DLDL-1	72-76	18-20	3-4	≤1	≥3.0	≤1.5	≥12
DLDL-2	65-68	25-30	3-4	≤1	≥3.0	≤1.5	≥12