BaGa4Se7 Crystals
$3000.00
≥1 Piece/Pieces
Send Inquiry
CHENGDU DIEN PHOTOELECTRIC TECHNOLOGY CO., LTD
You might also like
Product description
High-quality crystals of BGSe (BaGa4Se7) is the selenide analogue of the chalcogenide compound BaGa4S7, whose acentric orthorhombic structure was identified in 1983 and the IR NLO effect was reported in 2009, is a newly developed IR NLO crystal. It was obtained via the Bridgman–Stockbarger technique. This crystal exhibits high transmittance over the wide range of 0.47–18 μm, except for an absorption peak at around 15 μm.
The FWHM of the (002) peak rocking curve is about 0.008° and the transmittance through a polished 2 mm thick (001) plate is around 65% over the wide range of 1–14 μm. Various thermophysical properties were measured on crystals.
The thermal expansion behavior in BaGa4Se7 does not exhibit strong anisotropy with αa=9.24×10−6 K−1, αb=10.76×10−6 K−1, and αc=11.70×10−6 K−1 along the three crystallographic axes. The thermal diffusivity/thermal conductivity coefficients measured at 298 K are 0.50(2) mm2 s−1/0.74(3) W m−1 K−1, 0.42(3) mm2 s−1/0.64(4) W m−1 K−1, 0.38(2) mm2 s−1/0.56(4) W m−1 K−1, along the a, b, c crystallographic axis respectively.
In addition, the surface laser damage threshold was measured to be 557 MW/cm2 using a Nd:YAG (1.064 μm) laser under conditions of 5 ns pulse width, 1 Hz frequency, and D=0.4 mm spot size.
BGSe (BaGa4Se7) crystal exhibits a powder second harmonic generation (SHG) response that is approximately 2–3 times that of AgGaS2. The surface laser damage threshold is about 3.7 times that of AgGaS2 crystal under identical conditions.
BGSe crystal has a large nonlinear susceptibility, and may have a broad prospect for practical applications in the mid-IR spectral region.It shows interesting terahertz phonon-polaritons and high nonlinear coefficients for terahertz generation.
Advantages for IR laser output:
Suitable for various pumping source (1-3μm)
Wide tunable IR output range (3-18μm)
OPA, OPO, DFG, intracavity/extravity, cw/pulse pumping
Important notice: Since this this a new type crystal, inside crystal may have few streaks, but we do not accept returnment due to this defect.
The FWHM of the (002) peak rocking curve is about 0.008° and the transmittance through a polished 2 mm thick (001) plate is around 65% over the wide range of 1–14 μm. Various thermophysical properties were measured on crystals.
The thermal expansion behavior in BaGa4Se7 does not exhibit strong anisotropy with αa=9.24×10−6 K−1, αb=10.76×10−6 K−1, and αc=11.70×10−6 K−1 along the three crystallographic axes. The thermal diffusivity/thermal conductivity coefficients measured at 298 K are 0.50(2) mm2 s−1/0.74(3) W m−1 K−1, 0.42(3) mm2 s−1/0.64(4) W m−1 K−1, 0.38(2) mm2 s−1/0.56(4) W m−1 K−1, along the a, b, c crystallographic axis respectively.
In addition, the surface laser damage threshold was measured to be 557 MW/cm2 using a Nd:YAG (1.064 μm) laser under conditions of 5 ns pulse width, 1 Hz frequency, and D=0.4 mm spot size.
BGSe (BaGa4Se7) crystal exhibits a powder second harmonic generation (SHG) response that is approximately 2–3 times that of AgGaS2. The surface laser damage threshold is about 3.7 times that of AgGaS2 crystal under identical conditions.
BGSe crystal has a large nonlinear susceptibility, and may have a broad prospect for practical applications in the mid-IR spectral region.It shows interesting terahertz phonon-polaritons and high nonlinear coefficients for terahertz generation.
Advantages for IR laser output:
Suitable for various pumping source (1-3μm)
Wide tunable IR output range (3-18μm)
OPA, OPO, DFG, intracavity/extravity, cw/pulse pumping
Important notice: Since this this a new type crystal, inside crystal may have few streaks, but we do not accept returnment due to this defect.
Send your inquiry to this supplier
Send Inquiry
Product Alert
Subscribe to your interested keywords. We will send freely the latest and hottest products to your Inbox. Don't miss any trade information.
Subscribe
Your use of this website constitutes acknowledgement and acceptance of our Terms & Conditions.
Copyright © 2009-2024 Bossgoo Co., Ltd. All rights reserved.