Dental Lab/ Zirconia Ceramic Blocks/CAD/CAM Aidite zirconia disk and blocks are the finest and most pure zirconia materials on the market, most of zirconia powder are from Tosoh Company Japan. We guaranty the quality the same as original brand in strength,translucency and homogeneity etc. we adopt the most advanced isostatic pressing equipment and large sintering furnace to guaranty a homogeneous density distribution. Zirconia Ceramic Blocks
* Fully compatible with Cercon System, Sirona System, Wieland System, Kavo System, Amann * Girrbach System,
* Zirkon Zahn Sytem, Manual System, etc.,
* Significantly reduce the usage cost of materials
* Variety and specifications upon enquiry request Notes:
Polished the appearance:
This depends on the machining progress which you have chosen. Please note the following:
1. Note the distances of the milling burrs running in the unit time, take it slowly.
2. Change the milling burrs in time
main feature: *First grade zirconia powder,HT&ST available *Made under COLD ISOSTATIC PRESSING AND MACHINING which gives a more uniform fit lifetime *High translucency and mechanical strength, reliable stability; Suitable for crowns & bridge, and anterior & posterior denture. *CE and FDA approved All shapes Dental Zirconia Blocks according to customer's requirement.
| Milling System | Specification |
Wieland Cad/Cam Mill System | | N/M | OD*H(mm) |
| AW98 | 98mm*10mm |
| AW98 | 98mm*12mm |
| AW98 | 98mm*14mm |
| AW98 | 98mm*16mm |
| AW98 | 98mm*18mm |
| AW98 | 98mm*20mm |
| AW98 | 98mm*22mm |
| AW98 | 98mm*25mm |
| AW98 | 98mm*28mm |
technical parameters
| |
Sintering density (densely sintered in high temperature) | (6.05±0.02) g/cm3 |
Chemical compositions | ZrO2+HfO2+Y2O3>99.0 wt% Al2O3<O.25 wt% |
Bending strength | ≥1100MPa |
Chemical solubility | 6.7µg·cm-2 |
| |
cytotoxicity | The grade of the cytotoxicity is 0 |
Short term systemic toxicity test –oral route | Has no systemic toxicity |
Delayed-type hypersensitivity | Has no sensitization |
| |