1 / 6
Model No. : | YHASA00151 |
---|---|
Brand Name : | YH |
Product description
using today's advanced twofold extrusion technology for one-off processing with a separate function in each layer: | |||
The surface material adopts the ASA high weather resistant engineering plastic . ASA is a ternary polymer made up of acrylonitrile, | |||
styrene and acrylate with outstanding durability, UV resistance and chemical corrosion resistance, which ensures the bright color and | |||
luster and superb durability and chemical corrosion resistance of the product; the sublayer material is the extremely tough | |||
polyvinyl chloride resin (PVC), which ensures strength while increasing rigidity. | |||
A. The surface material adopts the ASA high weather resistant engineering plastic. | |||
B. The sublayer material is the extremely tough and lightproof modified PVC. | |||
Featured by its lasting color, UV resistance (ensuring an extremely long service life), easy cleaning, light weight, | |||
water resistance, toughness, heat insulation, sound insulation, corrosion resistance, wind resistance, shock resistance, hail resistance, | |||
contamination resistance, environmentfriendliness, fire resistance, insulation and easy installation, ASA Spanish Style.Tile Roofing provides | |||
advanced solutions for the workshops with corrosive substances and the areas with heavy acid rain as well as the durability of roofing |
Model | YH-SPANISH/ASA | ||
Thickness | 2.8±0.1mm | 3.0±0.1mm | |
Length | customized(must be according the times of 219mm) | ||
Overall width | 1050mm | ||
Effective width | 960mm | ||
Purlin spacing | 660mm | ||
Weight | 2.8mm: 5.6±0.1kg/m2 | 3.0mm: 6.0±0.1kg/m2 | |
Container Load capacity | Thickness | SQ.M./20 FCL (21 Tons) | SQ.M./40 FCL (26 Tons) |
2.8mm | 3500 | 4300 | |
3.0mm | 3300 | 4100 | |
Item | Content | Result | Standard |
Environment | Pollution or environment friendly | No asbestos and Environment friendly Recycling material | GB6566-2001, A standard good for Environment |
Heat distortion temperature | Under 70.0°C | No change | GB/T1634-2004 |
Vicat softening temperature | Under 75.2°C | No Softening | GB/T1633-2000 |
Hard to burn | B1 Grade | Oxygen index:35 | GB/T2406-1993 |
Vertical Burning | FV-0 | FV-0 | GB/T2408-1996 |
horizontal Burning | FH-1 | FH-1 | GB/T2408-1996 |
Impact Resistance | no crack | 0/10 | GB/T8814-2004 |
Density | 1.75-1.95 | 1.79 | GB/T1033-1986 |
Corrosion-resistant | Acid (HCL,H2SO4,HNO3)5% | No change | QB/T3801-1999 |
Alkaline(NaOH)5% | No change | QB/T3801-1999 |
Heat-resistance | (72°C 6h) no deformation, no viscousness | High-low temperature change | ± 0.11% |
Cold-resistance | (-40.0°C,6h) no crack in surface | Fire-protection | Class B1 Retardant Building Materials |
Bending capability | 25mm | Vicat softening temperature | ≥ 75 °C |
Flexural load | 800N, no crack | Water absorption rate | ≤ 0.05% |
Fleural strength | 72MPa | Nail force | ≥ 46N |
Tensile strength | 30MPa | Chemical resistance properties | No reaction in salt,alkali( ≤ 60%) |