Product description
Safety Shoes Materials
Characteristic:High strength and cohesive force, good abrasion resistance
Application: Double density sole system for common safety shoes and one-step forming casual shoes, outsole
Shoe Sole Polyurethane Resins Typical properties of PU matrixName of products | Appearance |
Viscoscity (mPa·s/40℃) |
Density (g·cm-³/40℃) |
Package (kg) |
A-6170 | liquid | 1000-1400 | 1.01-1.02 | 18 |
B-8280 | Yellowish Transparent liquid or waxy | 600-1000 | 1.08-1.2 | 20 |
Polyester Polyol Isocyanate Materials preheat
A-6170: preheated at 50-60℃ for 6-8℃ hours
B-8280: preheated at 50-60℃ for 8-12 hours
Typical processing parameters & Reaction parameter
Mix ratio A+C/B
(By weight)
Cream time
(s)
End of Rise Time
(s)
Free Rise Foam Density
(g/cm³)
Mold Temperature
(℃)
Demold Time
(min)
Items
A/B Materials Temperatures(℃)
Parameter
40-45/40-45
sole
mid-sole
sole
mid-sole
40-50
100/69-71
100/77-79
6-8
6-7
Items
parameter
sole
mid-sole
45-55
3-5
0.60-1.0
0.23-0.27
The adding content of C-2 should be 300g±10g/18kg
The adding content of water and hardener should be changed according to the reality
Sole: H2O 0-30g/18kg Hardener 0-400g/18kg
Mid-sole: H2O 50-55g/18kg Hardener 0-600g/18kg
Xuchuan chemical established in 2007, company registered capital is RMB 500 million. The main products a