Product description
Characteristics
Iron based nanocrystalline alloys, such as iron, silicon, boron, niobium, copper, etc..
Cu and Nb of iron - based amorphous alloy containing above the crystallization temperature
of annealing, will form a very fine grain microstructure, grain size only 10-20 nm,
this non amorphous alloy by special annealing crystallization and the formation of crystalline
material called nanocrystalline alloy. Nanocrystalline materials with high saturation magnetic
induction intensity, high permeability, low coercivity, low loss and good stability, high
strength toughness and wear resistance and corrosion resistance and other excellent properties,
as has the best price performance ratio of nano crystalline alloy material in metallic soft
magnetic materials, can replace the silicon steel, permalloy and ferrite, become the ideal
material of high frequency transformer, transformer, inductance components.
product performance
1K107 iron based nanocrystalline Ribbon
saturation induction density Bs/T 1.25
saturation magnetostriction constant λs 27*10^-6
Curie temperature Tc(℃) 560
Density D (g/cm^3) 7.2
crystallizing temperature Tx(℃) 510
electrical resistivity ρ(Ωm²/m) 130
hardness HV(kg/mm^2) 880
Thickness um 29-35
1K107B iron based nanocrystalline
Ribbon
Thickness um 0.020-0.025
filling factor σ ≥0.80
magnetic displacement B/T ≥1.12
coercive force Hc(A/m) ≤2.0
Iron loss P0.5T/20k /(W/kg) ≤25
Iron loss P0.3T/100k /(W/kg) ≤100
Permeability u(1khz) ≥70000
Permeability u(10khz) ≥60000
Permeability u(100khz) ≥10000
Curie temperature Tc(℃) 570
Continuous Working Temperature℃ -50--120
saturation magnetostriction constant λs <2*10^-6