TOP-Stabilizer-01 Integral blade stabilizer near bit stabilizer API 7-11. Size: 6"--36"
2..Material: AISI 4145H,4145 MOD,AISI 4340,AISI 4140-4142, Non-mag material
API 7-1 near bit stabilizer and string stabilizer
Delivery Condition of semi-finished stabilizer or reamer forgings:
Heat treated by water quenching and tempering,rough machined to drawing dimensions, UT-Tested according to ASTM A-388
Mechanical property: Requirement:
Tensile Strength 140.000PSI Min
Yield Strength 110.000PSI (0.2% offset)Min
Elongation 13% Min
Reduction of Area 45% Min
CHARPY-V-N 40
Hardfacing for Stabilizer:
HF1000 Crushed tungsten carbide held in a nickel bronze matrix. The 3mm grain size ensures greater concentration of carbide which is ideal for soft formation drilling.
HF2000 Trapezoidal tungsten carbide inserts held in a sintered carbide nickel bronze matrix. This will give a greater depth of carbide coverage -- ideal for high deviation drilling in abrasive formations.
HF3000 Tungsten carbide inserts set in a power spray deposit ideal for abrasive formation. 97% bonding guaranteed, certified by ultrasonic report. Recommended for non-magnetic stabilizers.
TCI Tungsten carbide inserts (button type). The inserts have been developed to allow cold insertion and maintain close fit. A greater concentration of inserts on the bottom third of the blade and leading edge will increase surface contact to reduce wear in highly abrasive formations.
integral blade stabilizer, specifications:
HOLE
SIZE
|
BODY
OD.
|
FISHING NECKLENGTH
|
BLADE LENGTH
|
BLADE WIDTH
|
TONG SPACE
|
BORE |
OAL LENGTH
|
8 |
43/4
|
30 |
15 |
3 |
25 |
21/4
|
72 |
81/2
|
61/2
|
30 |
18 |
3 |
27 |
213/16
|
78 |
121/4
|
8 |
30 |
18 |
31/2
|
28 |
213/16
|
83 |
121/4
|
91/2
|
30 |
18 |
31/2
|
28 |
3 |
83 |
143/4
|
8 |
30 |
18 |
31/2
|
30 |
213/16
|
90 |
143/4
|
91/2
|
30 |
18 |
31/2
|
30 |
3 |
90 |
16 |
91/2
|
30 |
18 |
31/2
|
30 |
3 |
92 |
171/2
|
8 |
30 |
20 |
31/2
|
30 |
213/16
|
94 |
171/2
|
91/2
|
30 |
20 |
31/2
|
30 |
3 |
94 |
20-26 |
91/2-11
|
30 |
22 |
4 |
30 |
3 |
110 |