Model No. : | 1100 3003 3004 5052 5182 |
---|
Product description
Items | Standard | Results |
Panel thickness | 3mm ,4mm, 5mm,6mm |
|
Aluminum thickness | 0.21mm, 0.25mm, 0.30mm, 0.35mm, 0.40mm, 0.45mm, 0.50mm or as the client request |
|
Available coating | PE, PVDF |
|
Standard size | 1220*2440mm |
|
Max width | 1570 |
|
Max length | 6000mm |
|
Thickness of coating | ≥ 20um | 25um |
Glossiness Deviation | Glossiness≥70, tolerance ≤ 5
Glossiness<70, tolerance ≤ 10 |
1.1 |
Hardness of pencil | ≥ HB | 3H |
Flexibility of coating | ≤ 2T | 2T |
Adhesive | Not less than Grade1 | Grade 0 |
Impact strength | 50Kg.cm Without paint off and crack | Pass |
Boiling water resistance | (Boiling for 2h without change) | Unchanged |
Acid resistance | Immerse surface with5%HCI(v/v)for 24h without change | Unchanged |
Alkali resistance | Immerse surface with5%NaOH(m/m)for 24h without change | Unchanged |
Oil resistance | Immerse surface with 20# engine oil for 48h without change | Unchanged |
Solvent resistance(MEK) | Clean 100 times with butanone without change | Bottom unrevealed |
Cleaning resistance | ≥ 10000 times without change | Unchanged |
Abrasion resistance | ≥ 5L/um | 9 L/um |
Contamination resistance | ≤ 15% | ≤ 2.5% |
Density of surface | Specified value: ± 0.5Kg/m2 | 5.32Kg/m2 |
Bend strength | ≥ 100Mpa | 104Mpa |
Bend modulus of elasticity | ≥ 2.0×10 4 Mpa | 2.9× 104 Mpa |
Through resistance | ≥ 9.0kN | 9.8kN |
Cutting strenght | ≥ 28.0Mpa | 29 Mpa |
180 o peel strength | ≥ 7.0N/mm | 12.3N/mm |
Resistance to change of temperature | -40 0 C~80 0 C 20 cycles without change | Unchanged |
Heat deformation temperature | ≥ 105 0 C | 107 0 C |
Coefficient of heat expansion C -1 | ≤ 4.00×10 -5 0 | 1.34 × 10 -5 |
Salt fog resistance | Not less than Grade2 | Grade 1 |
Artificial resistance aberration(200h) | ≤ 3.0 | 0.77 |
Aging resistance Out of light(200h) | Not less than Grade2 | Grade 1 |
other aging characteristic(200h) | Grade 0 | Grade 0 |