ASTM B111 C71500 Cooper Nickel Alloy Seamless Tube
C71500 (CuNi30Mn1Fe) Copper Nickel 70/30 Tubes -ASTM B111
ASTM B111 C71500 Copper Nickel Tube is the best resistance of any of the copper alloys to impingement attack and to corrosion from most acids and waters. It is being used in severe corrosive conditions in which service lives longer than those of other copper alloys are desired.
C68700 ASTM B 111/B 111M establishes the requirements for seamless tube and ferrule stock of copper and various copper alloys up to 3 Vs in. [80 mm] inclusive, in diameter, for use in surface condensers, evaporators, and heat exchangers.
Copper or Copper Alloy UNS NO. |
Description |
C70600 |
90-10 Copper-Nickel |
C71500 |
70-30 Copper-Nickel |
Standard: ASTM B 111/B 111M
Description Name: ASTM B111 copper tubes, C71500 copper tubes, C71500 Copper-Nickel tubes and pipes, CuNi30Mn1Fe Copper Nickel tubes.
Size: 4mm to 90 mm
Wall Thickness: 0.5 to 10mm
Shape: Round
Length: Single random length/ Double random length or as customer’s actual request
Grade: C70600, C71500, C71640
Designation
Chemical Composition %
Cu
Sn
Al
As
Ni
Fe
Mn
Pb max.
Zn
C44300
70.0-73.0
0.9-1.2
–
0.02-0.06
–
0.06 max
–
0.07
Rem
C68700
76.0-79.0
–
1.8-2.5
0.02-0.06
–
0.06 max
–
0.07
Rem
C70400
Rem
–
–
–
4.8-6.2
1.3-1.7
0.3-0.8
0.05
1.0max
C70600
Rem
–
–
–
9.0-11.0
1.0-1.8
1.0max
0.05
1.0max
C71500
Rem
–
–
–
29.0-33.0
0.4-1.0
1.0max
0.05
1.0max
C71640
Rem
–
–
–
29.0-32.0
1.7-2.3
1.5-2.5
0.05
1.0max
Tensile Requirements:
Copper or Copper Alloy UNS NO.
Temper Designation
Tensile Strength
Yield Strength
Standard
Former
min ksi
min ksi
C44300
O61
annealed
45
15
C68700
O61
annealed
50
18
C70400
H55
light-drawn
38
30
C70600
H55
light-drawn
45
15
C71500
O61
annealed
52
18
C71640
O61
annealed
63
25
· C71500 (CuNi30Mn1Fe) Copper Nickel Tube specimens selected for test shall withstand the expansion shown in standard when expanded in accordance with Test Method B 153. The expanded tube shall show no cracking or rupture visible to the unaided eye.
· Hard-drawn tubes not end annealed are not subject to this test. When tubes are specified end annealed, this test is required and shall be performed on the annealed ends of the sampled tubes.
· Tubes for ferrule stock are not subject to the expansion test.
Flattening Test
· Test Method: Each test specimen shall be flattened in a press at three (3) places along the length, each new place to be rotated on its axis approximately one third turn from the last flattened area. Each flattened area shall be at least 2 in. in length. A flattened test-specimen shall allow a micrometer caliper set at three (3) times the wall thickness to pass freely over the flattened area. The flattened areas of the test specimen shall be inspected for surface defects.
· During inspection, the flattened areas of the test- specimen shall be free of defects, but blemishes of a nature that do not interfere with the intended application are acceptable.
· Tubes for ferrule stock are not subject to flattening test.
Residual Stress Test
· A residual stress test is required to be performed only for Copper Alloy UNS Nos. C70600, C71500, C71640.
· Unless otherwise specified, the producer shall have the option of testing the product to either the mercurous nitrate test, Test Method B 154, or the ammonia vapor test, Test Method B 858, as prescribed below.
Nondestructive Testing
Eddy-Current Test—Each C71500 (CuNi30Mn1Fe) Copper Nickel tube shall be passed through an eddy-current testing unit adjusted to provide information on the suitability of the tube for the intended application. Testing shall follow the procedures of Practice E 243.
Hydrostatic Test
Each Copper Nickel tube shall stand, without showing evidence of leakage, an internal hydrostatic pressure sufficient to subject the material to a fiber stress of 7000 psi [48 MPa] as determined by the following equation for thin hollow cylinders under tension. The tube need not be tested at a hydrostatic pressure of over 1000 psi [7.0 MPa] unless so specified.