1 / 1
Model No. : | AAAC Conductor |
---|---|
Brand Name : | taifa |
Product description
AAAC- 6201 Alloy Bare Aluminum
Applications Used as bare overhead conductor for primary and secondary distribution. Designed utilizing a high-strength aluminum alloy to achieve a high strength-to-weight ratio; affords better sag characteristics. Aluminum alloy gives AAAC higher resistance to corrosion than ACSR. Construction Standard 6201-T81 high strength aluminum conductors, conforming to IEC61089 Specification, are concentric-lay- stranded, similar in construction and appearance to 1350 grade aluminum conductors. Standard 6201 alloy conductors are similar to other alloy conductors commercially known as Ardival, Aldrey or Almelec. They were developed to fill the need for an economical conductor for overhead applications requiring higher strength than that obtainable with 1350 grade aluminum conductors, but without a steel core. The DC resistance at 20°C of the 6201-T81 conductors and of the standard ACSR of the same diameter are approximately the same. Conductors of the 6201-T81 alloys are harder and, therefore, have a greater resistance to abrasion than conductors of 1350-H19 grade aluminum.
Applications
Used as bare overhead transmission cable and as primary and secondary distribution cable. ACSR offers optimal strength for line design. Variable steel core stranding enables desired strength to be achieved without sacrificing ampacity.
Construction Aluminum alloy 1350-H-19 wires, concentrically stranded about a steel core. Core wire for ACSR is available with class A, B, or C galvanizing; ""aluminized"" aluminum coated (AZ); or aluminum-clad (AW) - please see our ACSR/AW spec for more information. Additional corrosion protection is available through the application of grease to the corer or infusion of the complete cable with grease.
Specifications ACSR bare conductor meets or exceeds the following ASTM specifications:
B-230 Aluminum Wire, 1350-H19 for Electrical Purposes B-231 Aluminum Conductors, Concentric-Lay-Stranded B-232 Aluminum Conductors, Concentric-Lay-Stranded, Coated Steel Reinforced (ACSR) B-341 Aluminum-Coated Steel Core Wire for Aluminum Conductors, Steel Reinforced (ACSR/AZ) B-502 Aluminum-Coated Steel Core Wire for Aluminum Conductors, Steel Reinforced (ACSR/AW) B-498 Zinc-Coated Steel Core Wire for Aluminum Conductors, Steel Reinforced (ACSR/AZ) B-500 Zinc Coated and Aluminum Coated Stranded Steel Core for Aluminum Conductors, Steel Reinforced (ACSR)
AAAC- 6201 Alloy Bare Aluminum
Section: mm2 |
Stranding: No./mm |
Diameter: mm |
D.C Resistance at 20oC |
Calculated breaking load: kN |
Current: A |
||||
70 oC |
80 oC |
90 oC |
|||||||
10 |
7/1.35 |
4.05 |
3.31596 |
2.80 |
59 |
70 |
79 |
||
16 |
7/1.71 |
5.13 |
2.06673 |
4.49 |
79 |
94 |
106 |
||
25 |
7/2.13 |
6.39 |
1.33204 |
6.97 |
104 |
124 |
140 |
||
35 |
7/2.52 |
7.56 |
0.95165 |
9.75 |
127 |
152 |
173 |
||
50 |
7/3.02 |
9.06 |
0.66262 |
14.00 |
159 |
191 |
218 |
||
70 |
7/3.57 |
10.71 |
0.47418 |
19.57 |
195 |
235 |
269 |
||
95 |
7/4.16 |
12.48 |
0.34921 |
26.57 |
234 |
285 |
326 |
||
120 |
19/2.84 |
14.20 |
0.27745 |
33.62 |
270 |
330 |
379 |
||
150 |
19/3.17 |
15.85 |
0.22269 |
41.88 |
308 |
378 |
436 |
||
185 |
19/3.52 |
17.60 |
0.18061 |
51.64 |
350 |
431 |
497 |
||
210 |
19/3.75 |
18.75 |
0.15913 |
58.61 |
377 |
466 |
539 |
||
240 |
19/4.01 |
20.05 |
0.13917 |
67.02 |
409 |
507 |
587 |
||
300 |
37/3.21 |
22.47 |
0.11181 |
83.63 |
466 |
581 |
675 |
||
400 |
37/3.71 |
25.97 |
0.08370 |
111.71 |
553 |
695 |
810 |
||
500 |
37/4.15 |
29.05 |
0.06689 |
139.78 |
631 |
798 |
933 |
||
630 |
61/3.63 |
32.67 |
0.05310 |
176.32 |
721 |
919 |
1078 |
||
800 |
61/4.09 |
36.81 |
0.04183 |
223.84 |
826 |
1061 |
1249 |
||
1000 |
61/4.59 |
41.13 |
0.03351 |
279.46 |
933 |
1209 |
1429 |