Zirconia beads

Properties and technique parameters

Main composition

Y2O3 4.5%   ZrO294.5%

Specific Density

6.0~6.05g/cm3

Bulk density

3.70 g/cm3

Resistance to Compression

>2KN(Φ2mm)

Hardness in Mohs

9

Wear Rate (g/kg.h)

<=0.01%

Grinding Ball Size

Φ0.3~50mm

Grinding cylinder size

Φ5×5, Φ7×7,Φ10×10,12.7×12.7, 20×20,

25×25,30×30

 Main character

1.High bulk density lead to high kinetic energy,higher grinding efficiency.Which is 3~4 times than that of traditional ceramic beads.

2.Low abrasion,high strength without crashing under high speed and prevention material from any contamination.

3.Good chenmical stablility,resisting any corrosive liquid.

4.Good sphericity and mobility,smooth surface,easy washing without any pores.

5.Low working cost,improving output and quality of material.

6.Wide application in high speed ,stick liquid and ultra fine-powder grinding.