thermoplastic building coating for road marking

Density /g/cm3

2.02

Softening Point/°C

103

Color and appearance of coating film

After drying , no wrinkle, spot , falling off, sticking to the wheel .And the color and shape of coating has not large differences to standard plate 

Cure time /minutes

3

Chromaticity Coordinates/(x,y)

X:0.318

Y:0.337

Compressive Strength/Mpa

15.4

Luminance Factor

0.80

Abrasion Performance/mg(200r/1000g reduce weight)

55.2

Content of glass beads(%)

22.6

Flow resistance

39

Low temperature Anti-cracking of coating layer

Keep 4h in -10°C ,and lay 4h in normal temperature as a circulation .And continuously do three circulations , no crack 

Heating stability

Keep 4h in 200~220°Cin agitating condition, no obviously yellowing, burnt , blocked

Density /g/cm3

1.95

Viscosity

139

Color and appearance of coating film

After drying , no wrinkle, spot , falling off, sticking to the wheel .And the color and shape of coating has not large differences to standard plate 

Cure time /minutes

10

Cover Rate(%)

98

Chromaticity Coordinates/(x,y)

X:0.311

Y:0.328

Compressive Strength/Mpa

13.9 -- 23°C±1°C

2.4 -- 50°C±2°C

Luminance Factor

0.83

Abrasion Performance/mg(200r/1000g reduce weight)

21.5

Anti-watering

No abnormal phenomenon dunking in water for 24h 

Anti-alkali

No abnormal phenomenon dunking in calcium hydroxide saturated solution for 24h 

Flexibility/mm

1

Solid Content/%

71.2