surface sizing agent

       surface sizing agent       There are several types of surface sizing agents, able to satisfy customer needs in very different conditions, welcome to contact us for technical consulating!      Surface sizing agent CZMJ-25   1. Introduction:  CZJ-25, one of AKD agents, is marked by waterproof, quick reaction and wide range PH (2~6) adaption. It is used in the process of coated white board paper, art paper, case board paper and paper board sizing.   2. Configuration:  

Appearance	White lotion
Relative density	1.02-1.05g/m3
Solid content	22±1%
Viscosity(25°C)	<30mpa.s
PH	3.0±1
Ionicity	cation

      Surface sizing agent CZMJ-01   1. Chemical composition: Styrene-acrylate emulsion   2. Technical parameters:

Appearance	Solid content  %	ionicity	Viscosity	PH value
Milky emulsion	30±2	anion	below45 mPa.s	5.5-6.5

  Surface strength agent CZM J- 02 1. Introduction:  Surface strength agent CZMJ - 02 is one of the latest polymerization ionic emulsion products.  The surface sizing efficiency is better than those anionic surface sizing agent ones for it has positive charges, while the fiber pulp represent negative charges which makes CZM-02 strong binding force and better retain with the pulp. It is used to improve the printability and increase the surface strength of paper.  Owning to its excellent sizing effect for the neutral pulp, it’s widely used in the surface sizing system of writing paper, copy paper, art paper and coated white board paper.   2. Configuration:

Appearance	White lotion
Solid content	25±1%
Viscosity(25°C)	<80mpa.s
pH value	3~5
Ionicity	Sight ion
Solubility	Soluble in water ,intermisible with starch

    The Characteristics of SAE Surface Sizing Agent   Surface sizing agent is the fastest growing, most widely used polymer surface sizing agent. It is mainly composed of styrene, acrylates and various functional monomer copolymerization. It features simple synthesis process, low viscosity, few foam, easy to use, good water resistant effect and very popular. According to its synthetic process, SAE can be divided into two kinds: First, microemulsion polymerization type: typical representative: BK -532. Our PSC - 330 and PSC - 430 belong to similar products. Through instrument analysis, we find that the performance characteristics of microemulsion polymerizationare are as follows: Strong cation, the intensity of electric charge (Zeta potential) reaches vover 45; b) The average particle size less than 100 nanometers, including a large number of 20-40 nanometer particles; c) High glass transition temperature, Tg value is beyond 40 ° C; Second, Ordinary emulsion polymerization: representatives: Ciba surface sizing, Synthesis and uprightness PSC - 100; Most domestic manufacturers adopt this technology, and its physical properties are as follows: Cationic (Zeta potential) is weaker than microemulsion polymerization, about 25 All  particles are beyond 50 nanometer. The average particle size is greater than 100 nm; Glass transition temperature is about 40 ° C;
  
    The sizing mechanism and influence of physical properties of surface sizing agent:    A) Sizing mechanism of surface sizing agent: SAE polymer molecules with a positive charge form a network of water resistant film through crosslinking reaction with starch. At the same time, SAE cationic combines with polymer fiber anion by attaching on the surface of paper. Thus SAE water resistant polymer crosslinked, starch chain, and fiber chain crosslinking network structure become a dense film.     B) The strength of Zeta potential is an important indicator of cationic surface sizing, which directly relates to the adhesion strength of surfacing sizing and starch. The adhesion strength is higher, the membrane strength is higher. This is also related to the adhesion strength of surfacing sizing and fiber. The binding force between them is stronger, the sizing loss is less. Then the adding quantity is less;  C) Particle size influences two aspects: first, in small particle size, polymer particles in emulsion is more, then omentum coating on the surface of paper is more dense; Second, small particle size means that under the condition of equal amount, water resistant particles are greater than surface area; So if required to achieve the same water resistance, small particle size means the adding amount decreases. Generally speaking, under the condition of same solid content, the adding amount of surface sizing agent in nano emulsion is much less.   Welcome to contact for technical consulting or samples!