RECTANGULAR CERAMIC MAGNETS

Specifications RECTANGULAR CERAMIC MAGNETS

AKA FERRITE MAGNETS

MANUFACTURED IN FULL COMPLIANCE WITH ISO STANDARDS

Ferrite Ceramic magnets wholesale    General Information
Ceramic magnets (Ferrite magnets) are sintered permanent magnets composed of Barium or Strontium Ferrite. This class of magnets, aside from good resistance to demagnetization, has the popular advantage of low cost. Ferrite magnets are very hard and brittle, and require specialized machining techniques. Moreover, they should be machined in an unmagnetized state. We are equipped to machine these materials to specifications. Anisotropic grades are oriented in the manufacturing direction, and must be magnetized in the direction of orientation. Isotropic grades are not oriented and can be magnetized in any direction, although some degree of greater magnetic strength will be found in the pressing dimension, usually the shortest dimension. Due to their low cost, Ferrite magnets enjoy a very wide range of applications, from motors and loudspeakers to toys and crafts, and are the most widely used permanent magnets today.
Manufacturing:
  Pressing and sintering involves pressing very fine ferrite powder in a die, and then sintering this pressed magnet. All fully dense Ferrite magnets are produced this way. Ferrite magnets can be wet pressed or dry pressed. Wet pressing yields better magnetic properties, but poorer physical tolerances. Generally, the powder is dry for grade 1 or 5 materials, and wet for grade 8 and higher materials. Sintering involves subjecting the material to high temperatures to fuse the pressed powder together, thus creating a solid material. Magnets produced through this process usually need to have some finish machining, otherwise surface finishes and tolerances are not acceptable. Some manufacturers extrude instead of press wet powder slurry and then sinter the material. This is sometimes done for arc segment shapes, where the arc cross-section is extruded in long lengths, sintered, and then cut to length.   Injection Molding: Ferrite powder is mixed into a compound and then injection molded in the same way as plastic. Tooling for this manufacturing process is usually very costly. However, parts produced through this process can have very intricate shapes and tight tolerances. Injection molded ferrite properties are either lower or about the same as grade 1 Ferrite.  
Surface Treatments   The corrosion resistance of Ferrite is considered excellent , and no surface treatments are required. However, Ferrite magnets may have a thin film of fine magnet powder on the surface and for clean, non-contaminated applications, some form of coating may be required.  
Magnetizing and Handling Ferrite magnets require magnetizing fields of about 10 kOe. They can be magnetized with multiple poles on one or both pole surfaces. No special handling precautions are required, except that large blocks of Ferrite magnets are powerful, and care should be taken to ensure that they do not snap towards each other.
Temperature Effects Up to about 840F, changes in magnetization are largely reversible, while changes between 840F and 1800 F are re-magnetizable. For all Ferrite magnets, the degradation of magnetic properties is essentially linear with temperature. At 350 F, about 75% of room temperature magnetization is retained, and at 550 F, about 50% is retained.
Common Applications for Ferrite Magnets Ferrite magnets are widely used in motors, magnetic couplings, for sensing, loudspeakers, holding-magnet systems, crafts, magnetic therapy, novelties, and toys.

Material:		Ferrite Permanent Magnet
Shapes:		Ring, disk, block ETC
Features:		Cost effective alternative to other magnetic materials, offers relatively high operating temperatures and good resistance to corrosion & demagnetization. However, it has lower energy levels (Br) and is brittle in nature.
Applications:		DC motors, Louder-speaks, Magnetic Separators, Automotive Sensors, Educations, etc.
Magnetic Performance
Grade	Remanence Br mT (kGs)		Coercive force HcB KA/m (KOe)	Magnetic energy product Max KJ/m3 MGOe	Equivalents
Y10T	200-218		125-145	6.5-8.0	C1
	2.00-2.18		1.57-1.82	0.8-1.0
Y25	360-370		135-150	22.5-25.3
	3.60-3.70		1.70-1.88	2.8-3.2
Y30	380-390		191-210	27-30
	3.80-3.90		2.40-2.64	3.4-3.7
Y33	400-410		175-195	30.0-31.5	C5
	4.00-4.10		2.20-2.45	3.8-4.0
Y35	410-420		220-235	31.5-33.0
	4.10-4.20		2.77-2.95	4.0-4.2
Y30BH	380-390		223-235	27.0-30.0	C8
	3.80-3.90		2.80-2.95	3.4-3.7
Y33BH	400-410		288-300	30.4-31.5
	4.00-4.10		3.62-3.77	3.8-4.0