Product name | PVC Foam Board | Raw Material | PVC | |
Size | 122*244,156*305,205*305cm | Thickness | 1-30mm | |
Color | White,blue,black,yellow,etc | Density | 0.38-0.9g/cm3 | |
Type | Free Foam ,Crust Foam ,Co-extrusion | |||
Tolerances | +/- 0.03 on densities -0 to +5mm on width | -0 to +10mm on length |
PHYSICAL PROPERTY OF PVC FOAM BOARD | |||||
Free Foam Board | Low-ratio foamed unplastistized poly vinyl chloride (PVC)-Free foam board | ||||
Items | Unit | Index | |||
A Type | B Type | C Type | |||
Thickness θ | mm | θ<3 | 3≤θ≤5 | θ>5 | |
Apparent Density | kg/m3 | ≤900 | ≤750 | ≤600 | |
Shore Hardness | - | ≥45 | ≥45 | ||
Tensile Strength | Mpa | ≥11 | ≥7 | ||
Breaking Elongation | % | ≥15 | ≥7 | ||
Impact Strength | kJ/M2 | ≥10 or not fracture | ≥10 or not fracture | ||
Vicat Softenting Point | ℃ | ≥70 | ≥70 | ||
Size Changes in the Rate of Heating | % | ±2.0 | ±2.0 | ||
Water Absorption | % | ≤1.0 | ≤1.0 | ||
| Flexural Strength | Mpa | ≥17 | ≥15 | |
Elastic Modulus in Eending | Mpa | ≥800 | ≥400 | ||
| Screw Grip Force | N | - | ≥800 |
Crust Foam Board | Low-ration foamed PVGU board-Crust foam board | ||||
Items | Unit | Index | |||
Apparent Density | kg/m3 | ≤900 | |||
Shore Hardness | - | ≥55 | |||
Tensile Strength | Mpa | ≥10 | |||
Breaking Elongation | % | ≥10 | |||
Impact Strength | kJ/M2 | ≥12 | |||
Vicat Softenting Point | ℃ | ≥70 | |||
Size Changes in the Rate of Heating | % | ±2.0 | |||
Water Absorption | % | ≤1.0 | |||
Flexural Strength | Mpa | ≥20 | |||
Elastic Modulus in Eending | Mpa | ≥600 | |||
Screw Grip Force | N | ≥800 | |||
|
|
|
|
|
|
Coextrusion | Low-ratio foamed unplastistized poly vinyl chloride (PVC)-Coextrusion | ||||
Items | Unit | Index | |||
A Type | B Type | C Type | |||
Thickness θ | mm | θ<4 | 4≤θ≤8 | θ>8 | |
Apparent Density | kg/m3 | ≤1000 | ≤900 | ≤700 | |
Shore Hardness | - | ≥65 | ≥60 | ||
Tensile Strength | Mpa | ≥15 | ≥7 | ||
Breaking Elongation | % | ≥10 | ≥10 | ||
Impact Strength | kJ/M2 | ≥15 or not fracture | ≥12 or not fracture | ||
Vicat Softenting Point | ℃ | ≥73 | ≥73 | ||
Size Changes in the Rate of Heating | % | ±2.0 | ±2.0 | ||
Water Absorption | % | ≤1.0 | ≤1.0 | ||
Flexural Strength | Mpa | ≥17 | ≥9 | ||
Elastic Modulus in Eending | Mpa | ≥800 | ≥400 |