PET film coating tape

Specifications pet film coating tape:Backing:green polyester film

Good solvent-resistant, no residual, fits for powder coating

Polyester film Tapes Specifications:
1) Backing thickness: 0.035mm
2) Total thickness: 0.065mm
3) Tensile strength: 135N/inch
4) Elongation: 60%
5) Adhesion: 6.5N/inch
6) Breakdown voltage: 6kV
7) Extended heat-resistance: 200oC (30min)
8) Insulation class: F155oC
9) Good solvent-resistant, no residual, fits for powder coating and coil wounding     Tape Size: 3" plastic core , 33m length, from 3mm width upward     Product description:   ZH-PG365G is based on polyester film, single sided coated with high-temp resistant adhesive   Product composition:                                               

Polyester film

Silicone pressure sensitive adhesive

                                        Physical Parameter

Item	Unit	Specification	Test methods	Notes
Color		green	Visual assessment
Backing thickness	mm	0.035	ASTM D-3652	±0.001mm
Total thickness	mm	0.065	ASTM D-3652	±0.002mm
Peeling strength	N/25mm	7.0~10.5	ASTM D-3330
Tensile strength	N/25mm	≥115	ASTM D-3759
Elongation at break	%	≥40	ASTM D-3759
Heat resistance	°C/30min	200
Length	m	33

          Product Features: With excellent heat resistance, high cohesive force, soft and tender, no residue after peeling off. Application ideals: Widely used as masking tape in the high temperature condition, ideal for powder coating, super high temperature baking varnish and electroplating industry and so on… Storage condition and Shelf life: The product should be stored in the ambient temperature, in the 20~80%RH. You can obtain the best properties within 12 months after product date. Notes All above  mentioned techniques are the average values obtained after our several testing by acknowledged and reliable testing methods. In order to ensure the correct selection and using of our products. Please make a through understanding both of the purposes and conditions on usage in advance ,or notify us to provide you with further explanation and service.