pet bottle preform manufacturer Product Description Our PET Preform Features: 1) 100% new material 2) High transparency 3) High toughness 4)Blowing Rate up to 99.8% 5)Low Defect Rate 6)Low cost Neck and application: PCO 28mm PCO 1810 And 1881 for CSD and mineral water PCO 28mm PCO 1810crystallized for hot fill 95 ℃ European neck finish 30/25,29/25 for water 38mm 3-start,2-start for milk and juice plus specially finished preforms for hot fill Preforms for the production of 1gallon,2gallon,3 gallon,5 gallon/ 19 liter PET bottles for water, oil and agricultural products Mold list:
Neck finish | Preform Wt.(gms) |
38mm 3start | 18,21,25,28,230,32,36,43,50,55,60,65,75,80g |
38mm 2start | 17,21,25,28,29,30,32,33,36,40,46,50,55,60,65,70,75,80,110 |
Neck finish | Preform Wt.(gms) |
46mm | 90g 106g 116g 130g 143g 170g 200g |
Neck finish | Preform Wt.(gms) |
28mm pco 1810 | 14,16,18,20,21,23,24,25,27,28,30,31,32,35,38,40,42,43,45,50,52,55,60,64,68g |
28mm pco 1881 | 11 13,15,17,19,21,23,24,25,27,30,35,38,43,45,50,58g |
28mm Crystallized 1810 | 22,23.25,27,28,29,45,54,64g |
Neck finish | Preform Wt.(gms) |
30/25mm | 14,15,16,17,18,20,21,22,24,25,26,28,30,34 36 38,43g 50g 55g |
29/25mm | 13g 16g |
Neck finish | 55mm press neck and screw neck |
Preform Wt.(gms) | 180g 210g 250g 280g 300g 320g 350g 400g 430g 560g 660g 700g 730g 780g 800g |
Our Material
Packing and Shipping Delivery time: with 5-7days for MOQ after prepayment confirmed Payment terms: 30% deposit T/T before production, the balance before shipping. Package details: inner polybag,export standard outer carton Remark: above items can be negotiated
Blown Problem&Causes TROUBLE SHOOTING BLOWING PROCESS
Problem : Haze
Possible Causes : IV too low, Preform too hot, Low level crystallinity in preform
Problem : Pearlescence
Possible Causes : Preform too cold, Insufficient soak time, Improper preform design
Problem : Pearlescence in a Particular Section
Possible Cause : Affected section too cool
Problem : Thin Sidewalls
Possible Causes : Preform too hot, IV too low, excessive preform moisture, improper heating profile
Problem : Heavy neck area
Possible Causes : Preform too hot, IV too low, excessive preform moisture, improper heating profile, too much heat in bottom area, pre-blow air starting too early
Problem : Shelf life failure
Possible Causes : Preform too hot, IV too low, Excessive preform moisture, Improper heating profile
Problem : Heavy bottom area
Possible Causes : Preform too hot, IV too low, Excessive preform moisture, Improper heating profile, Too much heat in top area, pre-blow air starting too late
Problem : Drop Test Failure
Possible Causes : Preform too hot, IV too low, Excessive preform moisture, Improper heating profile, Too much heat in top area, Preblow air starting too late, Excessive gate crystallinity in preform
Problem : Top Load Failure
Possible Causes : Preform too hot, IV too low, Excessive preform moisture, Improper heating profile, Too much heat in top area, Preblow air starting too late
Problem : Creep
Possible Causes : Preform too hot, IV too low, Excessive preform moisture.
Problem : Localized Surface Imperfections
Possible Causes : Water in blow air, Contamination, Small un-melts in preforms