Surtek 3351 | ||
1 | Chemical base | Polyurethane |
2 | Color | Black |
3 | Density (DIN 53479) | 1.35±0.05 kg/l |
4 | Non-sag properties | Good |
5 | Cure mechanism | Moisture-curing |
6 | Tack-free time | 20~60 min |
7 | Rate of cure | ≥3 mm/24hr |
8 | Shore A hardness (DIN 53505) | 60±5 |
9 | Shear strength (without primer) | ≥1.5 N/mm2 |
10 | Tensile strength (DIN 53504) | ≥4 N/mm2 |
11 | Elongation at break (DIN 53504) | ≥400% |
12 | Tear strength (DIN 53515) | ≥10 N/mm |
13 | Glass transition temperature (DIN 53445) | -45°C approx. |
14 | Service temperature (continuous) Short – term (up to 48 hrs) | -40°C to +90°C 130°C |
NOTE: at 23°C and 50% relative humidity | ||
Surtek 3355 | ||
1 | Chemical base | Polyurethane |
2 | Color | Black |
3 | Density (DIN 53479) | 1.30±0.05kg/l |
4 | Non-sag properties | Good |
5 | Cure mechanism | Moisture-curing |
6 | Tack-free time | 20~60 min |
7 | Rate of cure | ≥3 mm/24hr |
8 | Shore A hardness (DIN 53505) | 60±5 |
9 | Shear strength (without primer) | ≥2 N/mm2 |
10 | Tensile strength (DIN 53504) | ~ 5 N/mm2 |
11 | Elongation at break (DIN 53504) | 400% |
12 | Tear strength (DIN 53515) | ≥10 N/mm |
13 | Glass transition temperature (DIN 53445) | -45°C approx. |
14 | Service temperature (continuous) Short – term (up to 48 hrs) | -40°C to +90°C 130°C |
NOTE: at 23°C and 50% relative humidity | ||
Surtek 3356 | ||
1 | Appearance | Uniform Paste |
2 | Color | Black |
3 | Density | 1.25 ± 0.05 kg/l |
4 | Tack-free time* | 15~35 min |
5 | Rate of cure* | ≥3 mm/24 hrs |
6 | Work temperature | 5-35°C |
7 | Shore A hardness | ~ 60 |
8 | Tensile strength | ≥6 N/mm2 |
9 | Elongation at break | ~ 300% |
10 | Shear strength | ≥4 N/ mm2 |
11 | Tear strength | ≥10 N/ mm |
12 | Service temperature (continuous) Short – term (up to 48 hrs) | -40°C to +90°C 130°C |
NOTE: at 23°C and 50% relative humidity | ||
Surtek3358 | ||
1 | Appearance | Uniform Paste |
2 | Color | Black |
3 | Density | 1.25 ± 0.05 kg/l |
4 | Tack-free time* | 10~30 min |
5 | Rate of cure* | ~ 4 mm/24 hrs |
6 | Work temperature | 5-35°C |
7 | Shore A hardness | ~ 60 |
8 | Tensile strength | ≥ 7 N/mm2 |
9 | Elongation at break | ≥ 250% |
10 | Shear strength | ≥4 N/ mm2 |
11 | Tear strength | ≥10 N/ mm |
12 | Service temperature (continuous) | -40°C to +90°C |
Short – term (up to 48 hrs) | 130°C | |
NOTE: at 23°C and 50% relative humidity |