Low Cr Alloy Steel Mill Liners For Conch Cement Group With More than HRc50

Quick Details

1. Low Cr Alloy Steel Liners are designed for high impact value & abrasion performance.
2. More than HRC50, more than AK49J.

Low Cr Alloy Steel Liners for Conch Cement Mill Description:

1. Hardness difference from surface to center is less than HRc2.

2. Low Cr Alloy Steel Liners are designed for high impact value & high abrasion performance.

3. More than HRc50, AK49-88J.

In the recent 20 years, our liners have been widely used in large, medium and small ball mills in Chinese power generation, mining, cement, Chemical engineering and metallurgical industries and super fine pulverizing equipments. It is the only recommended liner product in the latest standard of the electric-power industry in China.

Technical Parameters

Wuxi Orient Anti-wear Engineering Co., Ltd.

Chemical Composition & Mechanical Property of Wear-resistant Castings

Item	Cr-Mo Alloy Steel I	Cr-Mo Alloy Steel II	Cr-Mo Alloy Steel III	High Cr white iron	High Cr Alloy Steel	High Manganese Steel	Ni-Hard cast iron
C	0.30~0.50	0.65~0.90	0.40~0.90	2.40~3.20	1.1~2.2	0.90~1.30	2.40~3.60
Si	0.50~1.20	≤0.75	0.70~1.20	0.60~1.20	0.60~1.20	≤0.08	≤0.80
Mn	0.40~1.20	0.50~1.20	0.60~1.00	0.50~1.00	0.50~1.00	11.00~18.00	≤2.0
Cr	1.70~2.50	1.50~2.50	4.00~7.00	12.00~30.00	11.00~30.00	1.50~2.50	1.5~10
S	≤0.04	≤0.06	≤0.04	≤0.04	≤0.04	≤0.04	≤0.15
P	≤0.04	≤0.06	≤0.06	≤0.06	≤0.06	≤0.06	≤0.15
Mo	≤0.5	≤0.5	≤0.5	0.10~3.0	0.10~3.0	≤1.0	≤0.10
Cu	0.10~0.60	≤0.25	0.20~0.40	0.10~1.00	0.10~1.00	-	-
Ni	≤0.50	≤0.30	0~0.30	0~0.30	0~0.30	-	3.3~10
Re	≤0.02	≤0.02	≤0.02	-	-	-	-
Equivalent Specifications	DL/T 681-1999 GB/T26651-2011	AS 2074 L2B Mod	DL/T 681-1999	GB/T 8263-1999 AS 2027 Cr27 AS 2027 CrMo 15/3 AS 2027 CrMo 20/2/1 ASTM A532 Class III type A 25% Cr ASTM A532Class II type B 15% Cr-Mo BS 4844 3E DIN1695 NFA32401.		GB/T 5680-1998 DL/T 681-1999 JIS G 5153-1999 ASTM A 128 DIN GX120Mn12 AFNOR:Z120Mn12	GB/T 8263-1999 AS 2027/Ni-Cr1-550 AS 2027/Ni-Cr2-500 AS 2027/Ni-Cr4-500 AS 2027/Ni-Cr4-600 AS 2027/Ni-Cr4-630 ASTM A 532 1-A,B,C,D ASTM A 532 2-A,B,C,D,E ASTM A 532 3-A
Material Type	Martensite Steel	Martensite or Pearlitic Cr Mo Steel	Martensite Steel	Martensite matrix		Austenitic Mn Steel	-
Hardness	HRc≥48	HB470 & HB 321~370	HRc≥50	HRc≥56		HB≤300	HRc≥56
Impact Value	Ak≥40J	-	Ak≥10J	Ak≥4J		Ak≥80J	-

Our foundry has complete melting, heat treatment and test equipments, such as mid-frequency induction electrical furnaces, quenching and tempering furnaces, blast shot, spectrometer, Rockwell and Brinell Hardness tester, impactor, UT tester and metallographic microscope. We achieved the certificate of quality management system ISO 9001:2008. We have been exporting castings to oversea markets, such as Brazil, Australia and South Africa.