Product Description Application of Liquid Silicone rubber for concrete moulding: 1. Resin crafts, unsaturated resin crafts. 2. Poly resin crafts, candle crafts, plastic crafts. 3. Making molds forgypsum,GRC,concrete,Artificial stone products molding,Wax casting. 4. Decoration building mold making. 5. Lighting & candles crafts,stationery gifts,crafts industry. 6. Casting for Statue,Buddha, Christmas ornaments,sculptures,figures,etc Features of Liquid Silicone rubber for concrete moulding: 1. Two part of liquid fluid: liquid white silicone and curing agent. 2. Cure at room-temperature within 4-8 hours, but all performance will act perfectly when it cure within 2 - 4 hours. 3. Good fluidity and excellent operation. 4. Good resistance to weather, temperature, aging, acid. 5. Excellent tear strength, comfortable duplication times. Datasheet: Base and Curing Agent Mixture (100:3 by weight) in 25 °C (77F) testing.
Typical general characteristics | Inspection Method | Value |
Product data (Catalyzed A+B) | S815 | S820 | S825 | S830 | S835 | S840 |
Hardness | Shore A | 15±2 | 20±2 | 25±2 | 30±2 | 35±2 | 40±3 |
Mix Ratio | A:B | 100:3 | 100:3 | 100:3 | 100:3 | 100:3 | 100:3 |
Color | / | White/translucent | White/translucent | White/translucent | White/translucent | White/translucent | White/translucent |
Pot life | 25 °C (77F) | 20-40mins | 20-40mins | 20-40mins | 20-40mins | 20-40mins | 20-40mins |
Curing time | 25 °C (77F) | 3- 5hrs | 3- 5hrs | 3- 5hrs | 3- 5hrs | 3- 5hrs | 3- 5hrs |
Viscosity | mPa·s | 8000± 3000 | 14000± 3000 | 15000± 3000 | 21000± 3000 | 18000± 3000 | 19000± 3000 |
Tear-Strength | KN/m | ≥25 | ≥28 | ≥28 | ≥28 | ≥25 | ≥23 |
Tensile -Strength | MPa | ≥3.8 | ≥4.5 | ≥4.8 | ≥4.8 | ≥4.2 | ≥4.0 |
Elongation | % | ≥500 | ≥500 | ≥500 | ≥450 | ≥400 | ≥300 |
Shrinkage | % | ≤0.2 | ≤0.2 | ≤0.2 | ≤0.2 | ≤0.2 | ≤0.2 |
Operation Instructions of Liquid Silicone rubber for concrete moulding:
RTV-2 liquid mold silicone rubber is a kind of flowing liquid, and it consists of two component, part a is a flow-able liquid silicone rubber, part B is the curing agent. 1. Firstly, after your previous work of dealing with the original model, take some liquid silicone rubber, add 2%~3% cuing agent of the amount of silicon and mix themevenly. 2. Then after vacuum-pumping the mixture, you can pour it into the mold frame. 3. The silicone mold will cured in 2~3 hours. Note: the time for vacuum-pumping should be less than 3-5mins, otherwise, once the silicone rubber has cross-link reaction during vacuum. it will not be operated.
Packaging & Shipping Part A(silicone):1kg/bottle, 5kg/drum, 25kg/drum, and 200kg/drum. Part B(catalyst):40g/bottle, 0.2kg/bottle, 1kg/bottle, and 2kg/bottle.