PRODUCT DETAILS
fecral alloy strip Fe-Cr-Al Alloy
Longer high temperature service life
Superior oxidation resistance
Higher rresistance heating resistance fecral alloy strip fecral resistance wire grade: OCr27AL7Mo2, OCr21AL6Nb, OCr25AL5, OCr23AL5, OCr21AL4, 1Cr13AL4. In the form of wire, ribbon and strip Wire: 0.018mm-10mm Ribbon: 0.05*0.2mm-2.0*6.0mm
Strip: 0.5*5.0mm-5.0*250mm
PRODUCT APPLICATION
resistance (fecral) wire application
FeCrAl alloy wire is typically used in industrial furnaces and home appliances. Examples of applications are elements embedded in ceramics for panel heaters, infrared heaters, warming plates, irons, ceramic pots, in cartridge heaters for liquid heating, storage heaters, in ceramic heaters for cooking plates, air guns, hobby kilns, radiators, in quartz tube heaters for space heating, toasters, toaster ovens, grills, industrial infrared dryers, coils on molded ceramic fibre for cooking plates with ceramic hobs. Heating elements
Industrial electrical furnace, oven
1. Introduction of fecral resistance wire FeCrAl
Iron-chromium-aluminium (FeCrAl) metallic alloy is a high temperature alloy which can be used up to 1400° C and is a popular material choice for industrial furnaces. 2. fecral resistance wire feature
1) Excellent resistance to oxidation under heating condition;
2) High resistance and long lifetime;
3) Low temperature coefficient;
4 )Good performance of anti-carburizing, the atmosphere and surface of sulfur pollution. 3. fecral resistance wire advantage
Fe-Cr-Al resistance alloy has a good corrosion resistance at high temperature.
Fe-Cr-Al resistance alloy is much cheaper than Nickel Chrome wire.
Fe-Cr-Al resistance alloy wires are widely used in industrial furnacess, household appliances and far-infrared devices.
Fe-Cr-Al resistance alloy surface useing temperature can be 1400 degree, (0Cr21A16Nb, 0Cr27A17Mo2 and so on). 4. Chemical composition and main properties
main characteristic of FeCrAl electric heating alloy wire |
Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 |
Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 |
Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune |
Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest |
| | | | | | Nb0.5 | Mo1.8-2.2 |
Max. continuous service temp. of element( °C ) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 |
Resistivity at 20ºC(μΩ@m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 |
Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 |
Thermal conductivity(KJ/m@h@ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | |
Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 |
Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 |
Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 |
Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 |
Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 |
Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 |
Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 |
continuous servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 |
Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite |
Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
PRODUCT PROCESS
TEST EQUIPMENT
PRODUCT PACKAGE
CERTIFICATES
Company Information WHY CHOOSE SZNK HIGH QUALITY RESISTANCE HEATING ALLOYS? All our raw material is made from prime material, not recycle material. We have more than 25 years experience in manufacturing resistance heating alloys. 1) We achieve consistent production from smelting to complete products, we are able to supply satisfactory products. 2) We have has the world's advanced level of German ALD - VIDP1000 - 8000KG vacuum induction furnace and wire drawing machines from Japan. 3) With our skilled spooling knowhows, we have successfully magnified the take - up weight on spool. For example, even a superfine wire of 0.04 mm in diameter can be wound and shipped on a 3 - 4 kg bobbin, thus immediately contributing to your productive efficiency. 4) In order to prevent a wire from loosening, we have introduced a developed tension controlled systems into our take - up machine and respooling machine. We think you can anticipate smooth despooling. 5) Rolling mill with 4 stands in tandem is applied to our ribbons (rolled wires) manufacturing. FAQ Q1.Do you attend exhibition every year? A .Yes Q2.Is there any discount of the nickel wire? A. Yes. Bigger quantity will get lower discount. Q3.Information needed if I want a quotation? A Name, Standard, Material Grade(Chemical Composition), Size Quantity, Weight. Q4. Can we visit your company/factory before place the order? A. Yes. Welcome anytime Q5: How does your factory do regarding quality control? A. Quality is priority. We always attach great importance to quality controlling from beginning to end.