Heating Application and Solid Conductor Type thermocouple Wire

Heating Application and Solid Conductor Type thermocouple Wire    NiCr-NiAl (Type K)  thermocouple wire NiCr NiSi (Type K) thermocouple wire finds the widest use in all base metal thermocouple, at temperature above 500°C.The main chemical composition of  positive leg NiCr (KP) are Ni≈90% and Cr≈10%; negative leg NiAl (KN) are Ni≈97% and Al≈3%. The operating temperature range is -200~1300°C(for short term) and 0~1100°C( for long term). Type K thermocouple wire has strong resistance to oxidation than other base metal thermocouple bare wire . It has high EMF against Platinum 67, excellent temperature accuracy, sensitivity and stability, with a low cost. It is recommended for oxidizing or inert atmospheres, but cannot be used directly in the following cases:
(1) Alternatively oxidizing and reducing atmosphere,
(2) Atmosphere with sulphur gases 
(3) Long time in vacuum
(4) Low oxidizing atmosphere such as hydrogen and carbon monoxide atmosphere    Fe-CuNi(Constantan)  (Type J)  thermocouple wire Fe-CuNi (type J)  thermocouple wire is also named Fe- Constantan thermocouple wire . The positive leg Fe(JP) is made by pure Iron, and the main chemical composition of negative leg Constantan (JN) is Cu: Ni≈ 55%: 45%. Although they are all called Constantan, JN does not give the same EMF output curve as EN and TN, it cannot be instead by other Constantan. The operating temperature range of type J thermocouple wire  is -210~1200°C, but it is usually used in the temperature range 0~750°C due to embrittlement of Iron. Type J thermocouple wire  has good resistance to oxidation and high EMF output against Platinum 67, with good temperature accuracy, sensitivity and stability. It is recommended for vacuum, oxidizing, reducing or inert atmospheres, but it can not be used in sulphurous atmosphere above 500°C.    NiCr-CuNi(Constantan) (Type E)  thermocouple wire NiCr- CuNi (type E)  thermocouple wire is also named NiCr- Constantan thermocouple wire . The main chemical composition of positive leg NiCr (EP) is Ni: Cr≈90:10; negative leg Constantan (EN) is Cu: Ni≈ 55%: 45%. Although EN, TN, JN are all called Constantan, EN and TN don not give the same EMF output curve as JN. EN and TN are able to interchange but they are not interchangeable with JN. The operating temperature range of type E thermocouple is -200~900°C. Type E thermocouple wire  has the largest EMF output and highest sensitivity, so it is ideal for measuring small temperature change. It also has good stability in the low temperature range up to 300°C, and good property of anti-corrosion in humidity atmosphere. It is recommended for oxidizing or inert atmospheres, but cannot be used directly in reducing atmosphere and atmosphere with sulphur gases.      Cu-CuNi (Constantan) (Type T)  thermocouple wire Cu-CuNi (type T) thermocouple wire is also named Cu- Constantan thermocouple wire. The positive leg Cu(TP) is made by pure Copper, and the main chemical composition of negative leg Constantan (TN) is Cu: Ni≈ 55%: 45%. Although EN, TN, JN are all called Constantan, TN and EN don not give the same EMF output curve as JN. EN and TN are able to interchange but they are not interchangeable with JN. The operating temperature range of type T thermocouple wire is -200~350°C, Due to the low resistance of oxidation that Copper has, it is not advisable to go beyond that range. Type T thermocouple wire  has good resistance to oxidation, high EMF output, with good temperature accuracy, sensitivity and stability. In the temperature range -200~0°C, it has better property, the year stability is less than ±3μV           Production Process :       Packaging & Shipping             Our Services   1,  market analysis supply 2,  OEM, ODM confidentiality 3,  24 hours online service 4,  product recommendation 5,  Box desgin service  as per your sample       Company Information   Jiangyin Chengxin Alloy Material Co,.Ltd was founded in 2003 , which is a leading manufacturer of heating resistance alloy material in china , the main process equipment reached the international level . The company worked out a complete ,mature production process of heating alloy :from smelting, steel rolling ,drawing, heating treatment to the finished product , and with chemical analysis dept , physical testing dept ect.    The company produces hundreds of types of products with the “REOU” brand, comprising over a thousand specifications under seven main categories, they are : copper-based low resistance heating alloys (CuNi1-CuNi44), precision resistance alloys (Karma, manganin and constantan), high resistance heating alloys (nickel-chromium alloy wire), thermocouple alloys (K, N, E, T, J type), thermocouple compensation wire alloys, PTC thermistor resistance alloy and specialty wire (pure nickel wire and corrosion-resistant (Monel) alloy) with wire,ribbon,stranded wire,bar, foil ,sheet .The products have stable physcial performance , high surface loading ,oxidation resistance ,high electrical resistivity and stable temperature coefficient of resistance ect , which are widely used in military project, aerospace, household appliances, heating wire, mechanical, electrical plant, temperature instruments, and many other fields. With the annual output capacity of 1500tons per year ,the quality of products as much as KANTHAL level or more better and become the designated supplier of many world-renowned brand.   The company has a group of senior professional technicians as a strong backing, equipped with advanced manufacturing processes to ensure uniformity and consistency of quality of product , cooperated with domestic famous universities to develop and maintain its leading position in the technology sector . In 2004, we got the ISO9001: 2000 quality management system certificate . the standard is effectively service to the product development , marketing management , raw material control , production , finished product inspection and product delivery ect .   Under the leadership of presiden Mr Xingdong Cao, the company developed rapidly in recent years , focus on technology strength in 2008 we successful developed the “wind power leaf mold electric heating system” and “wind power leaf hydraulic flip system” with production capacity of 500 sets/year , the reliability and safety of product met customer’s requirements .    In the future development ,our company always persist in “technological innovation, reliable quality, continuous improvement, customer satisfaction "business philosophy. We will supply best quality ,competitive price ,professional service to work with you and achieve win-win !