FC Magnesia-Carbon Bricks for EAF

                                 MgO-C Brick  For EAF   Manufacture:      1.Use the large crystal,fused magnesia and high-purity graphite as raw materials;     2. Make the phenolic resin as the binder, add variety of additives     3. To form by via high pressure formation 1000T above friction machine.  
Product features:     1. High refractoriness, excellent anti-oxidation, high strength, perfect thermal Stability;     2. Resist the erosion and spall, high abrasion- resistance strength , perfect ability Of anti-slag;      3. Difficult to oxidation and hydration, can be used for long time.
Product application:
    1. Used for the furnace wall and working lining of all kinds of furnace;     2. Used for the slag line for the ladle and EAF   Index:  

Grade		MgO (%)	C (%)	Apparent porosity(%)	Bulk density(g/cm3)	Cold crushing strength(MPa)	Hot temperature bending strength(MPa)≥1400°C30mm
RGMT-8	A	≥82	≥8	≤4	≥3.05	≥40	≥6
	B	≥80	≥8	≤5	≥3.03	≥40	≥5
	C	≥80	≥8	≤6	≥3.01	≥40	≥4
RGMT-10	A	≥80	≥10	≤4	≥2.98	≥40	≥6
	B	≥78	≥10	≤5	≥2.96	≥40	≥5
	C	≥78	≥10	≤6	≥2.94	≥35	≥4
RGMT-14	A	≥78	≥ 14	≤4	≥2.95	≥40	≥12
	B	≥77	≥14	≤5	≥2.94	≥40	≥8
	C	≥77	≥14	≤5	≥2.92	≥35	≥6
RGMT-18	A	≥74	≥18	≤4	≥2.90	≥40	≥12
	B	≥73	≥18	≤5	≥2.88	≥35	≥8
	C	≥73	≥18	≤5	≥2.85	≥35	≥6