Model No. : | MS113 |
---|---|
Brand Name : | Mega |
Product description
Test Item | Quantiy | Industrial Standard | Unit | Test Value | Test Result |
Size deviation | 10 | Ac=0, Re=2 | Pieces | 0 | Up to Standard |
Thickness | 10 | ±5 | % | -1.71~-1.5 | Up to Standard |
Deformation | 10 | Ac1=0, Re'=2 | Pieces | 0 | Up to Standard |
Edge Straightness | 10 | ±0.5 | % | ±0.2 | Up to Standard |
Water Absorption | 5 | 0.5<E≤3 | % | Average value:0.5 Single Value: 0.8 | Up to Standard |
Density | 3 | ≥2.5 | g/cm3 | 2.53~2.54 | Up to Standard |
Breaking Strength | 7 | ≥7.5mm ≥1000 | N | D>7.5mm 2804 | Up to Standard |
New Crack Modulus | 7 | Average Value≥30 Single Value≥27 | Mpa | Average value:38 Single Value: 37 | Up to Standard |
Fire Resistance | 1 | Graded by ABC from High to Low | --- | A1 | Up to Standard |
Anti-wear | 11 | level and rotation | --- | Level2 / 600r | Up to Standard |
Resistance to Thermal Shock | 5 | No crack after 10 cycle tests between 145°C ~ 15°C | --- | No crack | Up to Standard |
Resistance to Freezing | 10 | No crack or delamination after 100 cycle tests between 5°C ~ -5°C | --- | No crack, no delamination | Up to Standard |
Moisturized Expansion | 5 | ≤0.06 | % | Average value:0.1 Single Value: 0.02 | Up to Standard |
Resistance to Acid | 5 | Graded by ABC from strong to weak | Level | A | A |
Resistance to Alkali | 5 | Graded by ABC from strong to weak | Level | A | A |
Resistance to Stain | 5 | Classfied as level 5-level1 from the degree of pollution | Level | 5 | 5 |
Radioactivity | 2 | A class decoration materials: Ira ≤1.0, Ir ≤1.3 | --- | Ira=0.4 Ir=0.8 | A |
Australian Sandstone VS Mega Sandstone | ||
Feature | Australian Sandstone | Mega Sandstone |
Texture and Color | Natural color and texture, but big color variation of the Sandstone from different stone mines,installation effect is not uniformed. | Natural color and texture, small color variation of the Sandstone from different boards, installation effect is uniformed |
Stain resistance | A lot of pinholes make it high water absorption and easy to collect microorganisms, which cause it to darken or get moss, reduce its durability. | The surface is made of Inorganic facing materials,processed by Mega's patented techniques, giving it good self-clean and stain-resistance capacity and durability |
Installation | After cutting into boards, it's sandy and smooth,making it not suitable for gluing for safety concerns, but high cost for dry cladding. | Mega's Sandstone board is made of Inorganic facing material compounded with ceramic composited plate as a base. The embossed base is strong, and suitable for gluing |
Environment | Severe damage to the natural environment during the mining process. | No damage to the Nature as it is not exploited from stone mines |
Price | High price due to the high cost of mining and low yield rate. | Money efficient and affordable due to mass production and lower comprehensive cost |