Exquisite POM Machine Part for Machines
1. Materials: POM
2. Machining equipments: 3/4/5-axis CNC milling, CNC Turning, dilling etc.
3. Finished: Sand blasting, zinc/nickel/ chrome plated, Trivalent Chromate/Alodine, anodize, powder coating
4. Specifications: Machined according to client's drawing, the largest maching range is 1000mm × 550mm × 550mm
5. Precision: 0.005mm
6. Certification: ISO 9001
7. Drawing format: CAD / PDF/ DWG/ IGS/ STEP, etc.
8. Field: Precise medical devices, Industry automation, mechanical manufacturing etc.
The machining processes
1.Turning: For parts which have high surface requirement, wide-head cutters are better. When processing thin walled and soft material, cutters like knife are recommended.
2. Milling: When milling the surface, end-milling is more cost-effective than circular milling. For circular and forming cutter, it should have less than two cutter edges. In this case, the tolerance caused due to the edge vibration can be lowered to the minimum.
3. Sawing: Thin saws are usually used to saw thick parts to avoid the heating caused by friction. It would be better to use sharp and big sawblade.
4. Drilling: When drilling the solid materials, make sure to use sharp drill, otherwise the increasing pressure during drilling will cause material cracks.
The common document files accepted are : *.pdf/*.dwg/*.IGS/*.step/*.prt/*.sldprt Just send the drawings to us, we will handle the rest for you.
Images
Technical data sheet
PROPERTIES | Unit | Value |
I.Physical Properties | ||
Density | g/cm3 | 1.45 |
Water absorption 24hrs | % | < 0.3 |
II.Thermal Properties | ||
Heat deflection temperature - HDT/A | ºC | 110 |
Min. service temperature | ºC | -40 |
Max. service temperature | ºC | 100 |
Thermal conductivity at 23 ºC | W/(K*m) | 0.31 |
Coefficient of linear thermal expansion | 10-4*K-1 | 1.2 |
Flammability Rating(6mm thickness) | - | HB |
III.Mechanical Properties at 23ºC | ||
Tensile strength at yield | MPa | 63 |
Tensile strength at break | Mpa | - |
Elongation at break | % | 31 |
Modulus of elasticity after tensile test | MPa | 2,700 |
Modulus of elasticity after flexural test | MPa | - |
Hardness - Shore D |
|
83 |
Charpy impact strength | kJ/m2 | N. B. |
Friction coefficient |
|
0.35 |
IV.Electrical Properties at 23ºC | ||
Dielectric constant at 1 MHz | 106Hz | 3.8 |
Dielectric loss factor at 1 MHz | 106Hz | 0.005 |
Volume resistively | Ohm (Ω) * cm | >1013 |
Surface resisively | Ohm (Ω) | >1013 |
Dielectric strength | kV/mm | 40 |
Characteristics
-High surface hardness
-Good wear resistance
-Excellent machinability
-Nice self-lubricating properties
-Good dimensional stability
-Low water absorption
-Oil resistant
-Work under the temperature of -40-100ºC