ER70S - G welding wire ER70S-g
1,Standard GB/T 8110-2008: ER50-G AWS A5.18 ER70S-G JIS Z3312: YGW11 2,Specification ER70S - G welding wire , in addition to including the Si and Mn element, also added Ti elements, because of the Ti elements add can make the wire ball moving grain refinement, it has the stable arc, the relative amount of sparks and smoke production also greatly decreased, the welds and impact value also greatly enhanced.
Ti elements make molten droplets and weld metal grains are refined, the tensile strength, yield strength level close to 50 kg welding material classification standard limit, impact energy have increased significantly. 3,Application: Applied to the corresponding intensity level of carbon steel, low alloy steel structure of the steel parts, heavy plate, thickness of pipeline welding.
using a large current to weld, it can exert its superior performance, suitable for high current of thick plate butt and fillet welding and horizontal welding etc., often used in ships, Bridges, buildings, vehicle manufacturing, engineering machinery, such as welding occasion.
4,Feature ER70S -g is 500 Mpa grade carbon steel welding wire, containing Ti element, make the drop and the weld metal are refined grains, large current welding performance is good, good impact toughness, small spatter and smoke. greatly increase the welding efficiency. 5,Parameter 1)Size
Dia. | Spool size | weight |
φ0.6~1.6(mm) | D100mm D200mm D270mm D300mm K300mm | 1kg,5kgs,15 kgs,18 kgs,20 kgs |
2)Chemical Composition: (%) Item | C | Mn | Si | S | P | Ti+Zr | Cu | Value | ≤0.15 | 1.40-1.90 | 0.55~1.10 | ≤0.030 | ≤0.030 | ≤0.30 | ≤0.50 | | 0.058 | 1.44 | 0.73 | 0.012 | 0.009 | 0.17 | 0.124 | 3)Mechanical Property: Item | Rm (N/mm2) | ReL/Rp0.2 (N/mm2) | A(%) | KV2(J) | Data | ≥500 | ≥420 | ≥22 | ≥27(-30℃) | Value | 550 | 455 | 29 | 114,131,127 | 4)Reference current (DC+) Dia(mm) | Current(A) | CO2 (L/min) | φ0.8 | 50~100 | 15 | φ1.0 | 50~220 | 15~20 | φ1.2 | 80~350 | 15~25 | φ1.6 | 170~550 | 20~25 | Notice: 1. Must be removed before carry out the rust, oil, water and other impurities; 2. Pay attention to protect the purity of the gas and appropriate mixing ratio of the mixture; 3. The protective gas flow is controlled properly, about 20 ~ 25 l/min; 4. Control the length of wire stretched out between 15 ~ 20 cm. 1. Product Pictures - MIG welding wire ER70S-g 2. Packaging & Shipping 3. Production Process 4. Inspection 5. Product Applications Show the welding seams: 6. Our Factory 7. welding wire Certificates 8 Shanghai Eseen Fair Contact us: Send your inquiry to this supplier Send Inquiry
|