Er70s-6 Copper Coated Welding Wire/gasless mig welding wire Bronze mig welding wire ER70S-6 Basic Information A mild steel MIG welding wire er70s-6 containing higher silicon and manganese additions is designed to improve welding. The higher silicon content helps to reduce the molten metal surface tension, resulting in flatter weld bead profile with less spatter. Application Applicable for single pass and multi-pass welding of carbon steel and 500 MPa grade low alloy steel and is widely used in such fields as automobile industry, construction machinery manufacturing, ship building, metallurgical and mininge quipment manufacturing, bridge building, petrochemical industry and pressure vessel manufacturing, etc. Also applicable for high-speed welding of sheets and pipeline steel. Advantages 1. It has excellent mechanical performance such as fast melting rate, high depositing efficiency, stable arc, little spatter, beautiful seam. 2. The slag is fluid and when hardened it is compact and easy to remove. 3. It is suitable for all position welding of steel sheets and irregular joints even under unfavorable conditions. 4. High-speed welding of light gauge plate and pipe line steel. 5. Certificates: ISO9001,CE,TUV Features AWS Specification AWS A5.18 ER70s-6 Diameter
0.030''/0.035''/0.045''/1/16''(0.6-2.0mm) Weight
2 lb/10lb/33lb(0.9-15kgs) Welding Positions
Flat, horizontal, and vertical down Operating Range In Amps
.035” 100 – 130
.045” 140 – 180
1/16” 175 – 300 Welding wire information: Standard:AWS: ER70S-6/DIN SG2/BS A5.18/JIS YGM12, LY ER50-6, GB/T: ER50-6 Wire diameter: 0.8 /0.9/ 1.0 / 1.2 / 1.6 mm
Coil diameter: 220/270 /300mm
Weight: 1/5/15 kg
Winding: inline-layered, dense
Packing: wire on plastic reels in shrink film and a cardboard box Surface treatment:copper( Chemical coating of copper, advanced processing technology) Sheilding Gas:fully CO2 ; 75%-95% Ar + rest of CO2 ; 95% Ar + rest of CO2 Welding Process: Gas Metal Arc Welding -- GMAW / MIG Welding Process Kindly please CONTACT us for the BEST PRICE. Chemical Composition of Deposited Metal (%)
chemical composition of welding wire(%) | C | Mn | Si | S | P |
≤0.18 | ≤1.75 | ≤0.90 | ≤0.03 | ≤0.03 |
Mechanical Properties of Deposited Metal (%)
Mechanical Properties or Deposited Metal | Yield strength (Mpa) | Tensile strength (Mpa) | Elongation (%) | Akv ( J ) |
490-660 | ≥375 | ≥22 | ≥47 (-20 C) |
Free samples can be supplied for your evaluation !!
Packing & Payment Term & Delivery Time 1. Packing: In plastic spool or steel basket with 1kg/5kg/15kg net weight each, precision layer wound coiling, heat-shrieked film, sealing spool, outer carton,1.08mt(72ctns) per pallet. 2. Payment Term: By T/T,30% deposit and the balance against the copy of B/L. 3. MOQ:5 Tons 4. Delivery Time:15 days after confirming the order. We guarantee to delivery the goods on time and supply professional service!
Certificates:
Company Profile
Jinan Woerde Solder Co., Ltd., is a professional manufacturer of welding wires. Our main products are CO2 gas shielded solid wires, flux cored wires, submerged arc welding wires, high strength wires, stainless steel wires and so on. They are widely used in low carbon steel and low carbon alloy steel product welding in machinery manufacturing, pressure vessels, automobile manufacturing and shipbuilding industry.
Our company has advanced equipment, strong technical force, complete detection means and the quality is stable. We have passed ISO9001:2008 quality management system certification, and gained the China Classification Society Certificate of Works Approval. We have a good customer base and potential business development space in domestic and overseas markets. So far, our products have been exported to Europe, America and other countries in Asia and have been appreciated by customers.
Contect