Ordinary Portlanf Cement Clinker Technical Specifications
| |||||
ACCORDING TO CHINESE STANDARD GB/T21372-2008 |
|
| |||
TESTING ITEMS | UNITS | Result of Analysis | STANDARD | TEST STANDARD | |
MAGNESIUM OXID | MgO | % | 4.12 | 5.0MAX | GB/T176-1996 |
SULFAR TRIOXIDE | SO3 | 0.52 | 1.5MAX | ||
CALCIUM OXIDE | CaO | 64.92 | 63.0 MIN | ||
SILICON DIOXIDE | SiO2 | 21.52 | 18-24 | ||
ALUMINUM OXID | Al2O3 | 4.82 | 4.0-9.5 | ||
FERRIC OXIDE | Fe2O3 | 3.05 | 2.0-5.5 | ||
LOSS ON IGNITION | LOI | 0.32 | 1.5MAX | ||
TOTAL ALKALI | Na2O+0.658K2O | 0.57 | 0.60MAX | ||
INSOLUBLE RESIDUE | IR | 0.21 | 0.75MAX | ||
F-CaO | 1.32 | 1.5MAX | |||
3CaO·SiO2 | C3S | 58.41 | 37-65 | GB/T21372-2008 | |
2CaO·SiO2 | C2S | 17.92 | 15-37 | ||
3CaO·Al2O3 | C3A | 7.12 | 6-15 | ||
4CaO·Al2O3·Fe2O3 | C4AF | 8.92 | 7-18 | BY CALCULATION | |
Initial Setting Time | minute | 87 | 60MIN | GB/T1346-2001 | |
Final Setting Time | 128 | 300MAX | |||
Compressive Strength @ 03 days | Mpa | 32.5 | 25MIN | GB/T17671-1999 | |
Compressive Strength @ 28 days | - | 52.5MIN |