BRS acrylic emulsion mortar( polyacrylate emulsion )--Jinan TD double component

BRS acrylic emulsion mortar( polyacrylate emulsion ) Description According to the special process, acrylic emulsion water-proof&anti-corrosion mortar is made withacrylic waterproof latex, high-quality aggregates, special binding materials , of which acrylic emulsion is a kind of polymermodification molecule waterproof &anti-corrosion system; acrylic emulsion water-proof/anti-corrosive mortar with long life, convenientconstruction, more than 50 years life for long-term water soaking.The mortar has excellent performance of adhesion, crack resistance, frost resistance, seepage-proofing, anti-corrosive, chloride ion penetrationresistance, abrasion resistance, aging resistance etc. Application a. Concrete structure reinforcement, civil air defense facility waterproof plugging. b. Impermeability treatment of reservoir dam and harbor. c. Chemical corrosion building such as hot pool, refuse landfill, chemical warehouse, chemical tank, etc. d. Concrete repair of pavement, bridge floor, tunnel, and culvert. e. Impermeability treatment for roof, toilet, basement of industry and civil architecture. f. Steel structure and reinforced concrete waterproof. h. Available for direct construction on wet base surface, good binding power with various base material. Technical data  

Item	Standard	Detection index
Initial setting time	>45	300
Final setting time	<12	10
Compressive strength(Mpa)28d	≥30	40
Flexural strength(Mpa) 28d	≥3.0	4.5
Bonding strength with cement mortar(Mpa)28d	≥1.2	1.5
Impermeability pressure (Mpa) 28d	≥1.5	1.7
Water-absorption	≤5.5	3.5
Alkali resistance	no   cracking,no spalling
Heat resistance	no   cracking,no spalling
Frost-resistance	no   cracking,no spalling
Shringkage /%	no   cracking,no spalling
Notes: 1. Alkali resistance is tested in   saturated solution of Ca(OH)2 for 168 hours.
2. Heat resistance is tested in the   water of 100℃ for 5 hours.
3. Freezing resistance is tested in   15-20 below zero for 25 times.

     

The performance index of Acrylic   emulsion latex
NO.	Items	Standard index	Detection index	Test results
1	Viscosity	11.5-12.5(25℃, pas)	12	first   grade
2	Total solids content	39-41	40	first   grade
3	Density	≥1.056	1.06	first   grade
4	Stock Stability	5~40℃,no obvious precipitation in 3 months.
5	Appearance	milky   homogeneous emulsion.

  Dosage a. 2tons/m3. b. Mixture ratio, single component water to material ratio: 15%; two-components emulsion to powder ratio: 15%-20%. c. Actual usage depends on site construction envrionment and toughness of used parts baseplane. Technology index(reference executive standard: GB/T50212-2002).   Package and storage a. Packing specification 20kg/barrel or 50kg/barrel, dry powder mortar 25Kg/bag. b. Stocked in dry, ventilate, moisture proof and rain-proof place. 6 months warranty. Non-toxic, tasteless, non-radiation, according with environmental requirement, available for general cargo storage and transport.