Boats Yachts Resin

Specifications common unsaturated polyester resin with medium viscosity and high reactivity

Shanghai New Tianhe Resin Co., Ltd.   DS-196 DS-196 is a common unsaturated polyester resin with medium viscosity and high reactivity, applicable to the manufacture of common steel glass products, cooling columns, containers of dilute acid etc.   

Technical Indexes of Liquid Resin
Item	Unit	Value	Standard
Appearance		Transparent Sticky Thick Liquid	Visual
Acid Value	mgKOH/g	18-23	GB2895-82
Viscosity(25℃)	mPa.S	300-700	GB7193.1-87
Gel Time	min	7-11	GB7193.6-87
Non-Volatile	%	60-67	GB7193.3-87
Thermal Stability (80℃)	h	≥24	GB7193.5-87
Note: Gel Time is 25°C; in air bath; 0.5 ml cobalt isocaprylate solution and 0.5 ml MEKP solution were added into 50 g resin

 

Performance Indexes of Resin Casting Substance
Item	Unit	Value	Standard
Barcol hardness≥	Barcol	38	GB3854-1983
Tensile strength ≥	MPa	60	GB2568-1995
Tensile modulus ≥	MPa	3000	GB2568-1995
Elongation at break≥	%	2.5	GB2568-1995
Flexural strength≥	MPa	88	GB2570-1995
Flexural modulus≥	MPa	3100	GB2570-1995
Impact strength≥	KJ/m2	8.5	GB2571-1995
H.D.T ≥	℃	73	GB1634-1989
Note: Environmental Temperature for Experiment: 23±2°C; relative humidity: 50±5%

    Packing and Storing DS-196: Packed in metal pail of 220 KG net weight with shelf life of 6 months at 20°C at ventilated places; avoiding direct sunlight and heat or fire. Note: The data were tested according to GB standard. Influenced by many factors in the process of fabrication, necessary researches by user are not exclusive. Legally, no warranties for some performances of product are applicable to one specific use, and the rights to amend the materials are reserved.