Biodegradable PVA Resin For Sponge Sheet Fishing Mesh
PVA Water soluble bag are primarily made of Polyvinyl Alcohol (PVA or PVOH) and organic plastics. PVA is a bio-based, synthetic polymer that was first discovered in the 1920s. PVA is odorless, non-toxic, biodegradable, and water-soluble. It comes in solid resin granules that are converted into a thin film which then makes all types of bags and chemical pods such as washing machine pods and fertilizers.
POLYVINYL ALCOHOL 24-88(088-50)
1. Description of Product
Appearance: White Powder on Flake
Solubility: Stable in almost all organic solvents. Not dissolved in animal and plant oils and grease.
2. Application
Paper sizing agent
Warp sizing in textile
Adhesive
Raw material of polyvinyl alcohol panel and PVA thin film
Paint and Coatings
Medicine、cosmetic and functional materials
Emulgator and dispersing agent.
3. Specifications
a. Hydrolysis degree: 87.0%- 89.0%
b. Purity: ≥93.5%
c. Viscosity: 45.0-58.0mpa.s
d. Volatile:≤5.0%
e. PH:5~7
f. Ash:≤0.5%
4. Storage:The material is very stable with no risk of molding and deteriorating. Under dry condition. Indefinite when protected from moisture.
5. Dissolving Method: Pouring a certain amount of water into the dissolving tank, the water temperature should be below 30 ℃, then start the blender and pour into PVA slowly, the filling speed with PVA should be keep into 10 kilograms per minutes advisable. Confirm the PVA powder has fully dispersed (about 10-20 minutes) then heat the solution, and it can be completely dissolved when heat to 90 ℃ about 1 hour.
6. Method of analysis: Viscosity is measured in 4% aqueous solution at 20℃. By a Brookfield type viscosimeter. PH is measured in 4% aqueous solution at 20℃ Ash expressed as Na2O.
7.Package: 20kgs/bag 16mt per 20'fcl with pallet.