bimetal wearing plate I . Product mold introduction * HP100 (Low stress abrasive wear) HP100 hard-faced wear-resistant steel plate is suitable for the low stress, little impact abrasive wear or fine particles, minimal energy and small incident Angle erosion wear condition. Hard-facing layer main chemical composition of metal (Wt%)
C | Cr | B | Other |
3~5 | 20~28 | + | 4~8 |
Hard-facing layer hardness: 60-65HRC Wear resistant temperature: <500℃ * HP200 (Resistance to medium impact abrasive wear) HP200 hard-faced wear-resistant steel plate is suitable for the medium impact abrasive wear or rolling compaction wear condition under high pressure. Hard-facing layer main chemical composition of metal (Wt%)
C | Cr | Mo | Mn | Other |
2~5 | 20~26 | + | 1~3 | 2~5 |
Hard-facing layer hardness: >58HRC Wear resistant temperature: <500℃ *HP300 (Resistance to high temperature abrasive wear) HP300 hard-faced wear-resistant steel plate is suitable for high temperature abrasive wear and fine particles, small Angle, small energy impact wear conditions Hard-facing layer main chemical composition of metal (Wt%)
C | Cr | Nb | Mn | Other |
4~6 | 18~24 | 5~8 | 2~3 | 3~6 |
Hard-facing layer hardness: 60-68HRC Wear resistant temperature: <800℃ II Dimension
Model | Spec(mm) | Total Thickness | Size | Minimum curling radius |
HP100/ HP200/ HP300 | Base material + wearing layer | (mm) | (W+L)mm | (mm) |
5+3 | 8±0.5 | 1450×2000 | R≥300 |
6+4 | 10±0.5 | 1450×2000 | R≥300 |
6+6 | 12±0.5 | 1450×2000 | R≥300 |
8+6 | 14±0.5 | 1450×2000 | R≥360 |
10+6 | 16±0.5 | 1450×2000 | R≥400 |
12+6 | 18±0.5 | 1450×2000 | R≥400 |
8+7 | 15±0.5 | 1450×2000 | R≥360 |
10+7 | 17±0.5 | 1450×2000 | R≥360 |
10+8 | 18±0.5 | 1450×2000 | R≥360 |
12+8 | 20±0.5 | 1450×2000 | R≥400 |
Remark: 1. This minimum curling radius is subject to a wear-resisting layer turning inward , if wear-resisting layer turning outwards, the minimum curling radius shall be multiply by 2. 2. We can also supply the special specification and size according to customer requirement. |
III. Technical Specification l Havel hard-faced wear-resistant steel plate is adopted special technique that enable the hardness between the layers uniform(0.5mm), so as to effectively guarantee the whole wear layer has the same abrasive resistance. l Wear layer thickness tolerance: +0.5/-0.5mm. l The Mounting face warp degree of liner plate for Havel hard-faced wear-resistant steel plate :≤3mm/1000mm l Crack of Wear layer: evenly spaced, tiny crack, not widely expand. l Surface layer size: smooth, no obvious roughness. l Surface spray paint: uniform paint layer, no need putty to repair, keep the state of nature. l Cutting edge of wearing plate: four sides, linearity, no raw edges, good forming by using large plasma cutting machine. IV. Product pictures